Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 68.9 - 200 MPa | 10000 - 29000 psi | Average value: 120 MPa Grade Count:19 |
Overview of materials for Acetal Homopolymer, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Glass Fiber Reinforced". Each property range of values reported is minimum and maxim.. |
|||
Flexural Yield Strength | 36.0 - 200 MPa | 5220 - 29000 psi | Average value: 139 MPa Grade Count:102 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Flexural Yield Strength | 55.2 - 200 MPa | 8010 - 29000 psi | Average value: 112 MPa Grade Count:68 |
Overview of materials for Polycarbonate, Stainless Steel Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Stainless Steel Fiber". Each property range of values reported is minimum and maximum val.. |
|||
Flexural Yield Strength | 113 - 200 MPa | 16400 - 29000 psi | Average value: 160 MPa Grade Count:16 |
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%.. |
|||
Flexural Yield Strength | 155 - 200 MPa | 22500 - 29000 psi | Average value: 178 MPa Grade Count:4 |
Overview of materials for Nylon 66/6, 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are incl.. |
|||
Flexural Yield Strength | 75.0 - 200 MPa @Temperature -40.0 - 90.0 °C |
10900 - 29000 psi @Temperature -40.0 - 194 °F |
Average value: 136 MPa Grade Count:3 |
Overview of materials for Nylon 66, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Flexural Yield Strength | 62.1 - 200 MPa | 9000 - 29000 psi | Average value: 79.9 MPa Grade Count:14 |
Overview of materials for Nylon 612 with PTFE Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612 with PTFE Filler". Each property range of values reported is minimum and maximum values of app.. |
|||
Flexural Yield Strength | 180 - 200 MPa | 26100 - 29000 psi | ASTM D790 |
Chang Chun Plastic PBT3030 30% Glass Fiber Enforced PBT Information provided by Dowell Trading Company Ltd. |
|||
Flexural Yield Strength | 165 - 200 MPa | 23900 - 29000 psi | Average value: 178 MPa Grade Count:7 |
Overview of materials for Polyethylene Terephthalate (PET), Recycled, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Recycled, Glass Reinforced". Each property range of values reported is.. |
|||
Flexural Yield Strength | 16.0 - 200 MPa | 2320 - 29000 psi | Average value: 82.1 MPa Grade Count:285 |
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |