Polymer Property : Flexural Yield Strength = 69.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	69.0 MPa	10000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® S705 ABS (Europe-Africa-Middle East) CYCOLAC S705 is a new generation ABS plating grade, offering semi high heat with a good property balance for impact and flow. CYCOLAC S705 demonstrates excellent electroplatability and a good therma..
Flexural Yield Strength	69.0 MPa	10000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Faradex AS0029 ABS (Europe-Africa-Middle East) LNP* Faradex* AS-1002 FR is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: Flame Retardant, EM..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Rotuba H5 Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer.
Flexural Yield Strength	69.0 - 170 MPa	10000 - 24700 psi	Average value: 89.8 MPa Grade Count:7
Overview of materials for Polyphenylene Ether, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, PTFE Filled". Each property range of values reported is minimum and maximum values ..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Ineos Nova 3500 General Purpose Crystal Polystyrene (discontinued **) Good blending resin, Suitable for difficult to fill and thin wall molding, USP Class VIApplications: Cosmetic and medical packaging, Housewares, Consumer Electronic packaging, ToysExposure to gamma ..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Ineos ABS Lustran® 256 Extrusion, Blending (discontinued **) A natural, medium-flow, medium-impact extrusion grade of ABS. It is used for blending with other Lustran ABS virgin and regrind materials to optimize cost and performance.Properties tested in trans..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Plenco 5000 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **) Plaslok 5000 is the replacement material for the former Union Carbide BMM-5000. It is a two-stage, woodflour-filled phenolic molding compound having versatile molding performance and preheating cha..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Plenco 7000 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **) Plaslok 7000 is the replacement material for the former Union Carbide BMM-7000. It is a two-stage, woodflour-filled phenolic molding compound having versatile molding and preheating characteristics..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Plenco 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound (discontinued **) Plaslok 506 is a two-stage, mineral-filled phenolic molding compound. It is formulated for automotive ashtrays and for appliance applications such as utensil handles receiving repeated exposure to ..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Plenco 5303 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound (discontinued **) Plaslok 5303 is a two-stage, mineral and flock-filled phenolic molding compound designed for use in appliance, automotive and electrical applications. It can be molded by compression, transfer or i..
Flexural Yield Strength	69.0 MPa @Strain 3.50 %	10000 psi @Strain 3.50 %	ISO 178
FKuR Kunststoff BiogradeÂ® C 6509 CL Biodegradable Plastic Compound BIOGRADEÂ® are easy to process blends based on cellulose. BIOGRADEÂ® is composed mainly of natural resources. Based on cellulose, a product of the paper industry BIOGRADEÂ® has been especial..
Flexural Yield Strength	69.0 MPa	10000 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL STN15HF PPE+PS Automotive interiors. Improved flow characteristics/overall processing economy. 240F DTUL. High impact/good property retention after heat ageing.
Flexural Yield Strength	69.0 MPa	10000 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL STN15HF PPE+PS (Asia Pacific) Automotive interiors. Improved flow characteristics/overall processing economy. 240F DTUL. High impact/good property retention after heat ageing.
Flexural Yield Strength	69.0 MPa	10000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP VN001 Super Tough Nylon LNP* LUBRICOMP* VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant.
Flexural Yield Strength	69.0 MPa	10000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT (Europe-Africa-Middle East) LNP* LUBRICOMP* WI001 is a compound based on Polybutylene Terephalate resin containing Silicone. Added features include; Inernally Lubricated.
Flexural Yield Strength	69.0 MPa	10000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® 364 PBT (Asia Pacific) Designed for outdoor telecommunications enclosure applications.
Flexural Yield Strength	69.0 MPa	10000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics XenoyÂ® 364 PBT This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	69.0 MPa	10000 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP SH0430AC_BK1D466 PA12 4.3 specific gravity nylon 12, clean compound system
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Eastman DuraStar DS1000 Polymer, Natural Durastar DS1000 polymer has excellent appearance and clarity. Its most outstanding features are chemical resistance and excellent processing characteristics. Exposure to aromatic oils often causes c..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Eastman DuraStar DS1110UVI Polymer, Natural Durastar DS1110UVI polymer, contains an ultraviolet light stabilization package. It is recommended for indoor applications requiring enhanced color stability upon extended exposure to fluorescent li..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Eastman DuraStar MN610 Polymer, Natural Durastar MN610 polymer has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. MN610 has very ..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Eastman Eastar Copolyester BR003, Natural PCTA Copolyester EASTAR BR003 Copolyester contains a mold release additive. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabiliti..
Flexural Yield Strength	69.0 MPa	10000 psi	ISO 178
Eastman Eastar GN071 Natural PETG Copolyester EASTAR GN071 Copolyester is used for injection molding applications. It is sparkling clear, tough, chemical resistant, odor free, versatile, easy to work with and affordable. Cleaning solutions wi..
Flexural Yield Strength	69.0 MPa	10000 psi	Test specimens were injection molded by ASTM D1897; ASTM D790
Chevron Phillips K-Resin® BK13 Styrene-Butadiene Copolymer, Injection Molding Grade (discontinued **) Styrene-Butadiene CopolymerBK13 is an SBC developed specifically to have enhanced flow capabilities and improved stiffness over the KR01 grade. BK13 molded parts give excellent detail on rapid prod..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
PolyOne Lubri-Tech™ MP-000/15T Modified PPO - 15% PTFE (discontinued **) Data provided by PolyOne.
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Kleerdex Kydex® 1900 Acrylic/PVC Thermoplastic Sheet (discontinued **) Mid-temperature aircraft gradeApplications: This sheet product is designed for use in small aircraft interiors but also is appropriate for other applications where higher in-service temperatures may..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Plaslok 5000 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use. Plaslok 5000 is the replacement material for ..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Plaslok 7000 Black General Purpose Woodflour Filled Phenolic Molding Compound (discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 7000 is the replacement material for ..
Flexural Yield Strength	69.0 MPa	10000 psi	ASTM D790
Plaslok 5303 Black Electrical Grade Mineral/Flock Filled Phenolic Molding Compound (discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 5303 is a two-stage, mineral and floc..