Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Yield Strength | 39.2 MPa | 5680 psi | ASTM D790 |
Multibase Multi-Pro® 1012 C Polypropylene Calcium Carbonate Filler, 12% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
Flexural Yield Strength | 39.2 - 88.9 MPa | 5690 - 12900 psi | Average value: 72.0 MPa Grade Count:16 |
Overview of materials for PETG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PETG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Flexural Yield Strength | 39.2 MPa @Thickness 3.20 mm |
5690 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
LG Chemical HIPS 410AF PS, Flame Retardant Description: Injection Molding, PS, Flame RetardantApplication: Office Appliances (Parts of Printer or Copier)CAS: 9003-55-8, 25713-60-4 and 1309-64-4Information provided by LG Chemical |
|||
Flexural Yield Strength | 39.2 MPa @Thickness 6.40 mm |
5690 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL GP3202B PP+MF20% Description: Injection Molding, PP+MF20%, Good WeatherabilityApplication: Electrical, Electronic and Automotive Interior PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 39.2 MPa @Thickness 6.40 mm |
5690 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL GP3202Z PP+MF20% Description: Injection Molding, PP+MF20%, Good WeatherabilityApplication: Electrical, Electronic and Automotive Interior PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 39.2 MPa @Thickness 6.40 mm |
5690 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL HI5205 PP+MF20%, High Impact Description: Injection Molding, PP+MF20%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 26221-73-8 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 39.2 MPa @Thickness 6.40 mm |
5690 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL HI5302R PP+MF30%, High Impact Description: Injection Molding, PP+MF30%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 39.2 MPa @Thickness 6.40 mm |
5690 psi @Thickness 0.252 in |
30mm/min; ASTM D790 |
LG Chemical LUPOL HI5302RB PP+MF25%, High Impact Description: Injection Molding, PP+MF25%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 14807-96-6Information provided by LG Chemical |
|||
Flexural Yield Strength | 39.2 MPa | 5690 psi | ASTM D790 |
KKPC Kuhmo HF 430U Weather-resistant Flame Retarded HIPS Key features: Excellent weather-resistance, non-deca heat-resistance. Common Uses: TV and VCR housing, parts needing non-deca type.HIPS is a functional resin made by copolymerization of styrene mono.. |
|||
Flexural Yield Strength | 39.2 MPa @Thickness 6.40 mm |
5690 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
LG Chemical LUPOL TE5007B PP+Rubber, High Impact Description: Injection Molding, PP+Rubber, Low Density, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia , Rear Bumper Step)Information provided by LG Chemical |
|||
Flexural Yield Strength | 39.2 MPa | 5690 psi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® P301T20 PP, 20% Talc Filled Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Yield Strength | 39.2 MPa | 5690 psi | ASTM D790 |
Cheng Yu Plastic PE221 Flame Retardant LDPE |
|||
Flexural Yield Strength | 39.2 MPa | 5690 psi | ASTM D790 |
Cheng Yu Plastic BK1020 Electric Conducting LDPE |
|||
Flexural Yield Strength | 39.2 MPa | 5690 psi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® P301T20 PP, 20% Talc Filled Information from Shinkong Synthetic Fibers Corp. |