Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 27.6 MPa | 4000 psi | Type I, 51 mm/min; ASTM D638 |
PolyOne Maxxam™ FR PP FR 7C11 Polypropylene, Unspecified (PP, Unspecified) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CR350CL-02 Polypropylene, Random Copolymer, Clarified CR350CL-02 is a clarified, random copolymer specially designed for clear injection molding applications and is formulated with lube for excellent mold release.Potential Applications: Injection moldi.. |
|||
Tensile Strength, Yield | 27.6 - 119 MPa | 4000 - 17300 psi | Average value: 57.1 MPa Grade Count:3 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Carbon Black Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Carbon Black Filled". Each property range of values reported is m.. |
|||
Tensile Strength, Yield | <= 27.6 MPa | <= 4000 psi | |
TSE Industries Millathane® 28 Millable Polyester Polyurethane Rubber Millathane 28 has excellent resistance to gas (e.g., nitrogen) permeability as well as very good abrasion resistance and low temperature properties. This polyurethane rubber was designed for automot.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Chevron Phillips HiD® 9410 HDPE Blow Molding Resin
(discontinued **) Resin Type: Linear Copolymer; Blow Molding ResinCharacteristics: Medium Molecular Weight Distribution, Wide Range of Processing Conditions, Good Parison Uniformity, Good TrimabilityApplications:Phar.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Chevron Phillips HiD® 9412/HiD® 9413 with Antistat HDPE Blow Molding Resin
(discontinued **) Resin Type: Linear Copolymer; Blow Molding, Injection Blow Molding ResinCharacteristics: Medium Molecular Weight Distribution, Reduced Yellow Potential, Wide Range of Processing Conditions, Good Flo.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
LyondellBasell Petrothene® LR732001 High Density Polyethylene (Blow Molding Grade) ApplicationsThe PETROTHENE LR 7320 series of polyethylene resins exhibits an excellent balance of stiffness and environmental stress crack resistance. Typical applications include bottles for bleac.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
LyondellBasell Petrothene® LR734001 High Density Polyethylene (Blow Molding Grade) ApplicationsThe PETROTHENE LR 7340 series of polyethylene resins exhibits good stiffness and ESCR. Typical applications include bottles for household chemicals.Regulatory StatusThe base resin LR 73.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
M. Holland Company CP501 Polypropylene Impact Copolymer AntistaticImpact copolymerHigh flowGood impact resistanceNucleatedGood stiffnessApplications: FurnitureHousehold goodsOutdoor furnishingsToys |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
M. Holland Company CP910 Polypropylene Impact Copolymer AntistaticImpact copolymerHigh flowNucleatedSlipHigh stiffnessApplications: ContainersHousehold goodsThin-walled parts |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2 in/min (50 mm/min); ASTM D-638 |
Ineos B53-35H-011 HDPE Ineos B53-35H-011 is a high density polyethylene copolymer developed for blow molding applications. This product is recommended for use in applications which require a combination of high top load .. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2 in/min (50 mm/min); ASTM D-638 |
Ineos B53-35H-100 HDPE B53-35H-100 is a high density polyethylene copolymer developed for injection blow molding. Zinc Stearate is incorporated in the formulation as a release agent. It is recommended for use in applica.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2 in/min (50 mm/min); ASTM D-638 |
Ineos B54-25H-127 HDPE B54-25H-127 is a high density polyethylene copolymer developed for blow molding. It is recommended for use in applications which require a combination of high top load strength and good environmenta.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Ineos L12Z-01 Polypropylene Impact Copolymer Grade L12Z-01 is a nucleated and antistatic polypropylene copolymer with a medium melt flow rate that provides an excellent balance of stiffness and impact. It is especially formulated to help provi.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D 638 |
LyondellBasell Pro-faxâ„¢ RP320N Polypropylene Copolymer Description: Pro-faxâ„¢ RP320N is a barefoot polypropylene random copolymer designed for cast film packaging applications. Cast film made with this resin has exceptional clarity and gloss, as wel.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D1457 |
Greene Tweed Avalon® 44 PTFE, Mineral, Molybdenum Filled Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester |
Lord Adhesives Chemglaze® V209 Polyurethane Coating Chemglaze® V-Line polyurethane coatings are moisture curing aliphatic polyurethane coatings. They are used in product finishing applications on polyvinyl-chloride (PVC) and other plastics where m.. |
|||
Tensile Strength, Yield | >= 27.6 MPa | >= 4000 psi | ASTM D-882 |
Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.010" thick) T-100/T-200 Features/Benefits: Outstanding heat and chemical resistance; High dielectric strength; Anti-stick properties; Can be chemically etched for bondability; Applications include laminate rele.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2"/min; ASTM D638 |
A. Schulman POLYAXIS® PD8020 Polypropylene DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2" (50mm) per min; ASTM D638 |
Formosa Plastics Formolene® 2302E Impact Copolymer Polypropylene Impact Copolymer for Extrusion Applications Formolene® 2302E is a low flow, medium impact polypropylene copolymer designed for extrusion applications. It is a barefoot resin with a basic stabilizat.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2" (50mm) per min.; ASTM D638 Type IV |
Formosa Plastics Formolene® HB5502Z Blow Molding HDPE Hexene CopolymerApplications: Injection blow molded pharmaceutical packagingFormolene HB5502Z eliminates the need for including a mold release agent at each machine, by incorporating zinc stearate w.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 2"/min; ASTM D638 |
A. Schulman POLYAXIS® PD8020 Polypropylene DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Total PSI 825EX Polystyrene Polystyrene 825EX is a high impact polystyrene designed for high stiffness in extrusion/thermoforming applications. The balance of high stiffness and impact properties allow for light weighting of t.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | chs 2.0 in/min; ASTM D638 |
Diamond Polymers SBS 1031 Clear Styrene Butadiene Copolymer Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Dow 334.03 Developmental Performance Polypropylene Polymer DOW D 334.03 Developmental Performance Polypropylene Resin is a propylene-based resin intended for use in extrusion blow molded containers requiring improved impact resistance. Targeted end-use app.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Dow R7021-50RNA Polypropylene Random Copolymer Resin DOW™ R7021-50RNA Polypropylene Resin is a random copolymer designed for thin wall injection molding applications desiring high clarity.Main CharacteristicsGood impact propertiesExcellent opticsFast.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | 50 mm/min (2 in./min.); ASTM D638 |
Bapolene® PP5062 Polypropylene, Injection Grade Polypropylene injection impact copolymer with excellent color and processability. This resin offers a superior balance of stiffness and impact strength. This product meets the FDA requirements of .. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Asahi Kasei Thermofil P-9900-1760 Unreinforced, Heat Stabilized, Impact Modified Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Mistron Vapor Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
Spartech Soft Touch PPR Co-Extruded Polyolefin Skin/PPR Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |