Formosa Plastics Formolene® HB5502Z Blow Molding HDPE

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Formosa Plastics Corporation, USA
Trade Name Formolene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® HB5502Z Blow Molding HDPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hexene CopolymerApplications: Injection blow molded pharmaceutical packagingFormolene HB5502Z eliminates the need for including a mold release agent at each machine, by incorporating zinc stearate with the resin. This incorporation assures uniform consistent release properties. It may be used as an injection blow molding resin.Produced using licensor formulation for HHM 5502BZ. Licensor does not warrant or imply that this product meets their specifications for HHM 5502BZ.Meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Nominal properties reported herein were determined on compression molded specimens prepared in accordance with Procedure C of ASTM D1928. Physical properties are typical of product but do not reflect normal testing variance and therefore should not be used for specification purposes.Information provided by Formosa Plastics Corporation, USA.
Physical Properties Metric English Comments
Density 0.955 g/cc
0.0345 lb/in³
ASTM D1505
Environmental Stress Crack Resistance 35 hour
35 hour
Condition B, F<sub>50</sub>; ASTM D1693
45 hour
45 hour
Condition A (100% Igepal), F<sub>50</sub>; ASTM D1693
Melt Flow 0.35 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.35 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Condition E; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 27.6 MPa
4000 psi
2" (50mm) per min.; ASTM D638 Type IV
Elongation at Break >= 600 %
>= 600 %
2" (50mm) per min.; ASTM D638 Type IV
Flexural Modulus 1.38 GPa
200 ksi
ASTM D790
Thermal Properties Metric English Comments
Brittleness Temperature <= -118 °C
<= -180 °F
ASTM D746