Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Multibase Multi-Pro® 3019 CXUW Polypropylene Calcium Carbonate Filler, 30% by weight.Features:Gloss, High Impact Resistance, GoodUV Resistance, Good Forms:PelletsProcessing Methods:Injection MoldingUses:FurnitureLawn EquipmentInformation prov.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Petromont 1000 High Density Polyethylene Resin Petromont HDPE 1000 is a high density polyethylene copolymer resin produced using the Unipol® Process. This multi-purpose resin can be used on intermittent and continuous blow moulding machines to .. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Petromont 1002 High Density Polyethylene Resin Petromont HDPE 1002 is a blow moulding high-density polyethylene copolymer resin produced using the UNIPOL® Process. This multi-purpose resin can be used on intermittent and continuous extrusion bl.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2" (50mm) per min, Type IV; ASTM D638 |
Formosa Plastics Formolene® HP5221 Pipe HDPE
(discontinued **) High Density Hexene Copolymer Formolene® HP5221 is a high performance copolymer that is designed for the most demanding requirements of corrugated pipe applications. Formolene® HP5221 meets the re.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
LNP Lubricomp® FL-4410 Polyetherimide, Silicone Lubricant Additive
(discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
M. Holland Company CP850 Polypropylene Impact Copolymer Impact copolymerFast production cycleHigh flowHigh stiffnessApplications: ContainersHousehold goodsThin-walled parts |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2 in/min; ASTM D638 |
Ineos CP53-30 Polyethylene Copolymer CP53-30 is a high density polyethylene copolymer developed for corrugated piping applications. This product is recommended for use in applications that are required to meet AASHTO specifications M 2.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2 in/min.; ASTM D638 |
Ineos J50-200-178 HDPE A high density polyethylene copolymer. It has a narrow molecular weight distribution and is intended for the molding of screw caps dedicated to the packaging of carbonated beverages. This material m.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2 in/min; ASTM D638 |
Ineos T50-800-01 Polyethylene Copolymer This is a high density polyethylene copolymer having a narrow molecular weight distribution. It is intended for injection molding applications where a good balance of processability and end-use pro.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
LTL Color Compounds ColorRxâ„¢ PP2-1001A Antimicrobial Polypropylene Random Copolymer An approx. 10 melt Polypropylene random copolymer containing antimicrobial protection. Ingredients are not approved for biocompatibility or food contact applications.All information provided by LTL .. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
LTL Color Compounds ColorRxâ„¢ PP2-1002AF Food Grade Polypropylene Random Copolymer An approx. 10 melt Polypropylene random copolymer with FDA food contact approval and antimicrobial protection.All information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
LTL Color Compounds ColorRxâ„¢ PP2-1002ARX Biocompatible, Antimicrobial Polypropylene Random Copolymer A biocompatible( approx. 10 melt Polypropylene random copolymer for healthcare applications containing antimicrobial protection.All information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength, Yield | >= 26.9 MPa | >= 3900 psi | ASTM D 638 type IV |
Total 5202 HDPE, blow molding Applications: Bleach and detergents, industrial chemicals, industrial parts, packaging aggressive liquids, food packaging. Blow molding stock temperature 360 - 400°F Extrusion melt temperature 380 .. |
|||
Tensile Strength, Yield | >= 26.9 MPa | >= 3900 psi | ASTM D 638 type IV |
Total 5202LD HDPE, blow molding Applications: Bleach and detergents, industrial chemicals, industrial parts, packaging aggressive liquids, food packaging. Blow molding stock temperature 360 - 400°F Extrusion melt temperature 380 .. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2" (50mm) per min.; ASTM D638 Type IV |
Formosa Plastics Formolene® HB5202B Blow Molding HDPE Hexene CopolymerApplications: Bleach, detergent and chemical containers; Molded or formed industrial housings, shrouds, tanksFormolene HB5202B is designed for applications requiring excellent stiffn.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR Mistron Vapor Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Eastman Tenite 380A4000015 Cellulose Acetate Propionate, Clear, Trsp Applications:OphthalmicsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Eastman Tenite Propionate 360E0096916 Natural, Trsp Cellulose Acetate Propionate Plasticizer 16%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Eastman Tenite Propionate 380A2R30015 Natural, Trsp Cellulose Acetate Propionate Plasticizer 15%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Chevron Phillips Marlex® 9004 HDPE Injection Molding Resin Resin Type: Linear Copolymer, ASTM D 4976 Classification: PE 233, A 56700Characteristics: Moderate Flow, Excellent Impact Strength, Good Stiffness, Excellent ESCR, Moderate Shrinkage ResistanceAppli.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Chevron Phillips Marlex® 9006 HDPE Injection Molding Resin Resin Type: Linear Copolymer, ASTM D 4976 Classification: PE 233, A 56700Characteristics: Moderate Flow, Excellent Impact Strength, Good Stiffness, Excellent ESCR, Moderate Shrinkage ResistanceAppli.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
ExxonMobil HDPE HPA 020 Wire & Cable High Density Polyethylene Resin Product Description: HPA 020 is a HDPE grade for Medium/High Voltage power cable jacketing. The grade should be used in blends with LLDPE to improve ESCR. Sufficient Carbon Black or UV stabilizer sh.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
ExxonMobil Paxon™ AB50-003 Blow Molding Resin Product Description: AB50-003 is a blow molding grade high density polyethylene copolymer. This resin has very good stress crack resistance combined with high impact strength and rigidity.Availabili.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Dow C133-02 Polypropylene Impact Copolymer Resin OverviewDow C133-02 Polypropylene Resin is intended for use in extrusion, thermoforming, and extrusion blow molding applications where impact at refrigeration temperatures is desired. It is especia.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DMDA-8907 NT 7 High Density Polyethylene Resin DOW DMDA-8904 NT 7 is produced using UNIPOL™ process technology. It is intended for use in injection molding applications such as pails, industrial parts and other shipping containers. Information.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM Data |
Dow Prevail® 3100 ABS + Polyurethane PREVAIL® 3100 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Aaron Industries AAROLENE® ARPE HD 300-2 Black Crate High Density Polyethylene Compounded Resin, Crate Grade AAROLENE® ARPE 300 Series Polyethylene Compounded Resin HDPE, Black Crate GradeFeatures: A high density Polyethylene compound, pre-colored black, specifically designed for all crate applications. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N774 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | 2 in/min.; ASTM D638 |
Ineos J50-2000-119 HDPE HDPE J50-2000-119 is a high density, narrow molecular weight polyethylene copolymer intended for applications requiring a glossy surface finish and reasonably good impact strength and rigidity. It i.. |
|||
Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
Techmer ES HiFill FR® HDPE FR-HB Availability: North AmericaForms: PelletsFeatures: Flame RetardantInformation provided by TP Composites, Inc. |