Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 210 MPa | 30500 psi | ASTM D638 |
Nylene® PA6/6 Glass Filled 5143 HS Nylon 6/6 43% Glass Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527, ASTM D638 |
Nilit Nilamid B3 H G8 40% Glass Fiber Reinforced PA6 Description: Nilamid B3 H G8 is a product that combines outstanding strength and stiffness with good moldability and good impact strength. It is widely used for structural applications.Key character.. |
|||
Tensile Strength, Yield | >= 210 MPa @Strain 0.200 % |
>= 30500 psi @Strain 0.200 % |
|
Industeel SIRIUS 800 Heat Resistant Alloy Description: The SIRIUS® 800, H and H+ grades are three variants of a high chromium and nickel austenitic alloy which combines good corrosion and creep resistance. SIRIUS® 800 is employed at t.. |
|||
Tensile Strength, Yield | >= 210 MPa @Strain 0.200 %, Temperature 98.9 °C |
>= 30500 psi @Strain 0.200 %, Temperature 210 °F |
|
H.C. Starck Ultra 76 Alloy (Ta 2.5%W) Benefits: Significantly improved corrosion resistance in HCl and H2SO4 acids.Minimized hydrogen embrittlement rates compared to standard NRC®76Up to 100 times lower in HCl acidUp to 10 times low.. |
|||
Tensile Strength, Yield | 210 MPa @Strain 0.200 %, Temperature 980 °C |
30500 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Yield | 210 MPa @Strain 0.200 %, Temperature 540 °C |
30500 psi @Strain 0.200 %, Temperature 1000 °F |
|
Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 210 MPa @Strain 0.200 % |
30500 psi @Strain 0.200 % |
Annealed prior to test |
Special Metals BRIGHTRAY® Alloy B Electrical Resistance Alloy A nickel-iron-chromium electrical-resistance alloy for use at operating temperatures up to 2010°F (1100°C). It contains rare-earth additions for increased oxidation resistance, especially und.. |
|||
Tensile Strength, Yield | 210 MPa @Strain 0.200 %, Temperature 550 °C |
30500 psi @Strain 0.200 %, Temperature 1020 °F |
Annealed prior to test |
Special Metals BRIGHTRAY® Alloy C Electrical Resistance Alloy A nickel-chromium electrical-resistance alloy for use at operating temperatures up to 2100°F (1150°C). It contains rare-earth additions for increased oxidation resistance, especially under co.. |
|||
Tensile Strength, Yield | 210 MPa @Temperature 550 °C |
30500 psi @Temperature 1020 °F |
Annealed prior to test |
Special Metals NIMONIC® Alloy 75 A nickel-chromium alloy with good mechanical properties and oxidation resistance at high temperatures. Used for sheet-metal fabrications in gas-turbine engines, for components of industrial furnace.. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp RF00ASXP PA6.6 (Europe-Africa-Middle East) LNP* THERMOCOMP* RF00ASXP is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regi.. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF00ASXS PA6.6 (Europe-Africa-Middle East) LNP* Thermocomp* RF00ASXS is a compound based on PA 66 resin containing Glass Fiber. Added features include: Heat Stabilized. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ASTM-D638 |
Polyram Polytron A35B01 Nylon 66, Chemically Coupled 35% Long Fiber A CHEMICALLY COUPLED 35% LONG FIBER GLASS REINFORCED BLACK NYLON 6.6 HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | dry; ISO 527 |
Ter Hell Plastic Terez® PA 6.6 HT 7110 GF 41 FL-HF/2 Polyamide 66 Copolymer, 41% Glass Fiber Description: Partly aromatic Polyamide 6.6 Copolymer, 41% glass fiber reinforced and flame retardants.Application:Stiff molding parts with high stiffness by outstanding thermal stability, reduced w.. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
Polyram PlusTek PA310G8BK10 Nylon 6.6 for injection Molding, 40% Glass Fiber Reinforced, Heat Stabilized Heat stabilized, 40% Glass fiber reinforced Nylon 6.6 for injection molding applications. Approved and listed by NSF/ANSI 61 International.Information provided by Polyram. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
Polyram PlusTek PB202G50BK39 Nylon 6, 50% Glass Fiber Reinforced, UV and Heat Stabilized 50% Glass fiber reinforced, UV and heat stabilized Nylon 6. Approved and listed by NSF/ANSI 61 International.Information provided by Polyram. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
Polyram PlusTek PB318G9 Nylon 6 for Injection Molding, 45% Glass-fiber Reinforced, UV Stabilized 45% Glass-fiber reinforced Nylon 6, UV stabilized for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
Polyram PlusTek RA314G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized 50% Glass fiber reinforced, heat stabilized Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | 5 mm/min; ISO 527 |
Eurostar Staramide RF00ASXP PA66, 50% Glass Filled, Injection Molded Staramide RF00ASXP is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 G 50V S3)Information provided by Eurostar. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | 5 mm/min; ISO 527 |
Eurostar Staramide RF00ASXS PA66, 50% Glass Filled, Injection Molded Staramide RF00ASXA is a 50% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ASTM D638 |
E-Polymers TEKAMID® TA250G60W , 62% Glass Fiber Reinforced PA66, DAM High strength, weather resistanceInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | >= 210 MPa | >= 30500 psi | |
AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 210), SAE J2340 Type 210 B Information provided by AK Steel |
|||
Tensile Strength, Yield | >= 210 MPa | >= 30500 psi | |
AK Steel Cold Rolled Carbon Steel, Bake Hardenable (BH 250) Information provided by AK Steel |
|||
Tensile Strength, Yield | >= 210 MPa | >= 30500 psi | |
AK Steel Cold Rolled Carbon Steel, Dent Resistant (DR 210), SAE J2340 Type 210 A Information provided by AK Steel |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® KR 4355 G7 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r.. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | 50 mm/min; ISO 527-1/-2 |
BASF Ultramid® KR 4355 G7 BK 00564 35% Glass Filled PA6/6T (Dry) Description: 35% glass-fiber reinforced product for injection-molding; high toughness, strength and stiffness, low water absorption, high melting point (295°C [563°F]). The mechanical properties r.. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | Dry; ASTM D638 |
Asahi Kasei Leona® 14G33 33% Glass Filled Nylon 66 Enhanced strength and stiffness; with 33% GF. Superior heat aging resistance, fatigue resistance, and creep resistance.Applications:Mechanical and electrical parts, engine mounts and other under-the.. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | 50mm/min; ISO 527 |
BASF Ultramid® A3EG7 35% Glass Filled PA66 (Dry) Ultramid A3EG6 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. |
|||
Tensile Strength, Yield | 210 MPa | 30500 psi | ASTM-D638 |
Polyram Polytron A35N01 Nylon 66, Chemically Coupled 35% Long Fiber A CHEMICALLY COUPLED 35% LONG FIBER GLASS REINFORCED NATURAL NYLON 6.6 HEAT STABILIZED FOR INJECTIONInformation provided by Polyram Ram On Ind. |
|||
Tensile Strength, Yield | 210 MPa @Strain 0.200 %, Temperature 550 °C |
30500 psi @Strain 0.200 %, Temperature 1020 °F |
Solution Annealed prior to test |
Special Metals INCONEL® Alloy HX A nickel-chromium-iron-molybdenum alloy with outstanding strength and oxidation resistance at temperatures to 2200°F (1200°C). Matrix stiffening provided by the molybdenum content results in high.. |
|||
Tensile Strength, Yield | 210 MPa @Strain 0.200 %, Temperature 550 °C |
30500 psi @Strain 0.200 %, Temperature 1020 °F |
Annealed prior to test |
Special Metals INCOLOY® Alloy 020 A nickel-iron-chromium alloy with additions of copper and molybdenum. It also contains niobium for stabilization against sensitization and resultant intergranular corrosion. The alloy has excellen.. |