Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 136 MPa | 19700 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Stat-kon WEF42 PET/PBT LNP Stat-Kon WCF-1006 is a compound based on PET/PBT resin containing carbon and glass fiber reinforcements.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 136 MPa | 19700 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK LNP* THERMOCOMP* LF003 is a compound based on Polyetheretherketone resin containing 15% Glass Fiber. |
|||
Tensile Strength, Yield | 136 MPa | 19700 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK (Asia Pacific) LNP* Thermocomp* LF003 is a compound based on Polyetheretherketone resin containing Glass Fiber. |
|||
Tensile Strength, Yield | 136 MPa | 19700 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 136 MPa | 19700 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific) LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 136 MPa | 19700 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF006EUC PA 66 LNP* THERMOCOMP* RF006EUC is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include Easy Molding, UV Stabilized. |
|||
Tensile Strength, Yield | 136 MPa @Temperature -40.0 °C |
19700 psi @Temperature -40.0 °F |
ISO 527 |
BASF Ultramid® 8200 HS PA 6 (Dry) Description: Ultramid 8200 HS is a heat stabilized, medium viscosity, PA6 injection molding homopolymer, exhibiting resistance to sink-mark formation in thick sections, and improved toughness over c.. |
|||
Tensile Strength, Yield | 136 MPa | 19700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Stat-kon PX98038 PA 6 (Europe-Africa-Middle East) LNP* STATKON* PX98038 is a compound based on PA6 resin containing Carbon Fiber, Glass Fiber, Flame Retardant. Added features include : Flame Retardant, Electrically Conductive, Heat Stabilized.This .. |
|||
Tensile Strength, Yield | 136 MPa | 19700 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Verton MV00ASUV_WH9D703 PP Preliminary data for 50% Long fiber single color pellet filled PPThis data was supplied by SABIC-IP for the Americas region. |