SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp LF003E PEEK (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* LF003E is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| 1.39 g/cc | 0.0502 lb/in³ | ASTM D 792 | |
| Linear Mold Shrinkage, Flow | 0.0079 cm/cm @Time 86400 sec |
0.0079 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| 136 MPa | 19700 psi | ASTM D 638 | |
| Tensile Strength, Yield | 125 MPa | 18100 psi | ISO 527 |
| 136 MPa | 19700 psi | ASTM D 638 | |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527 |
| 3.1 % | 3.1 % | ASTM D 638 | |
| Elongation at Yield | 2.4 % | 2.4 % | ISO 527 |
| 3.0 % | 3.0 % | ASTM D 638 | |
| Tensile Modulus | 6.93 GPa | 1010 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 199 MPa | 28900 psi | ASTM D 790 |
| 209 MPa | 30300 psi | ISO 178 | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 8.54 J/cm @Temperature 23.0 °C |
16.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 54.0 kJ/m² @Temperature 23.0 °C |
25.7 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 31.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 325 °C | 617 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 328 °C @Thickness 3.20 mm |
622 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 244 °C | 471 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 258 °C @Thickness 3.20 mm |
496 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Petroquimica Triunfo Trithene® TX 7001 LDPE - High Molecular Weight
- PolyOne Edgetek® PS-30CF/000 Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced (discontinued **)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Hi-Sil 243 LD Filler
- SABIC Innovative Plastics ULTEM 1285 PEI
- Westlake Plastics Tefzel® 2181 ETFE
- A. Schulman POLYBATCH™ Grey 8899 Concentrate Based In Polyethylene
- CPC - Vycom SANATEC® Sanitary Cutting Boards High Density Polyethylene
- Fainplast Compounds CTS 55/1 Flexible PVC, Extrusion Modified with Rubber
- ExxonMobil Bicor™ 25 ARW OPP Film
- Arkema Group LOTADER® AX 8900 Terpolymer Ethylene - Acrylic Ester - Glycidyl Methacrylate
Copyright © lookpolymers.com All Rights Reserved