SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK (Asia Pacific)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP LF003 PEEK (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* LF003 is a compound based on Polyetheretherketone resin containing Glass Fiber.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ASTM D792
1.39 g/cc
0.0502 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0079 cm/cm

@Time 86400 sec
 0.0079 in/in

@Time 24.0 hour
 ISO 294
0.0080 cm/cm

@Time 86400 sec
 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Time 86400 sec
 0.010 in/in

@Time 24.0 hour
 ASTM D955
0.010 cm/cm

@Time 86400 sec
 0.010 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
ISO 527
136 MPa
19700 psi
ASTM D638
Tensile Strength, Yield 125 MPa
18100 psi
ISO 527
136 MPa
19700 psi
ASTM D638
Elongation at Break 2.3 %
2.3 %
ISO 527
3.1 %
3.1 %
ASTM D638
Elongation at Yield 2.3 %
2.3 %
ISO 527
2.9 %
2.9 %
ASTM D638
Tensile Modulus 6.93 GPa
1010 ksi
1 mm/min; ISO 527
7.446 GPa
1080 ksi
50 mm/min; ASTM D638
Flexural Strength 199 MPa
28900 psi
ASTM D790
209 MPa
30300 psi
ISO 178
Flexural Modulus 6.274 GPa
910.0 ksi
ASTM D790
7.00 GPa
1020 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.54 J/cm
16.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 54.0 kJ/m²
25.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 14.0 J
10.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 48.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 26.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
48.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 30.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 17.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
31.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 17.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 325 °C
617 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
328 °C

@Thickness 3.20 mm
 622 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 244 °C
471 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
258 °C

@Thickness 3.20 mm
 496 °F

@Thickness 0.126 in
 unannealed; ASTM D648