Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 720 - 860 MPa | 104000 - 125000 psi | |
Materion Brush 60™ HT Information supplied by Brush Wellman Engineered Materials.Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 96%Stress Relaxation afte.. |
|||
Tensile Strength, Yield | 715 MPa @Strain 0.200 % |
104000 psi @Strain 0.200 % |
|
Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 720 MPa @Strain 0.200 % |
104000 psi @Strain 0.200 % |
|
Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Yield | 715 MPa @Strain 0.200 % |
104000 psi @Strain 0.200 % |
|
Haynes 230® alloy, 10% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Tensile Strength, Yield | 715 MPa @Strain 0.200 %, Temperature 650 °C |
104000 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 720 MPa @Strain 0.200 % |
104000 psi @Strain 0.200 % |
|
Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 720 MPa @Strain 0.200 %, Temperature 650 °C |
104000 psi @Strain 0.200 %, Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 105 A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater.. |
|||
Tensile Strength, Yield | 720 MPa @Strain 0.200 %, Temperature 550 °C |
104000 psi @Strain 0.200 %, Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 115 A precipitation-hardenable nickel-chromium-cobalt alloy with an addition of molybdenum for solid-solution strengthening. It is similar to NIMONIC alloy 105 but has higher levels of aluminum and tit.. |
|||
Tensile Strength, Yield | 720 MPa @Strain 0.200 %, Temperature 650 °C |
104000 psi @Strain 0.200 %, Temperature 1200 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy PK33 A nickel-chromium-cobalt alloy that is precipitation hardenable and also contains a relatively high (7%) level of molybdenum for solid-solution strengthening. It has an exceptional combination of h.. |
|||
Tensile Strength, Yield | 718 MPa | 104000 psi | Material as cured; RT |
Hexcel® HexPly® 922-1/35%/G926 180°C Curing Epoxy Matrix 5H satin/370g/m2 carbon fabric: FVC=60%Information provided by HexCel |
|||
Tensile Strength, Yield | >= 720 MPa @Strain 0.200 % |
>= 104000 psi @Strain 0.200 % |
|
CLAL-MSX NICLAFOR® 1000 TH2 Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
Tensile Strength, Yield | 720 MPa | 104000 psi | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 10% Cold Reduction, Heat Treated Heat Treatment 5 hours at 482°C. The strength, elongation, and hardness values are specific to this heat treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High .. |
|||
Tensile Strength, Yield | 717 MPa @Strain 0.200 % |
104000 psi @Strain 0.200 % |
|
Carpenter BioDur™ CCM Plus™ Medical Implant Alloy, Annealed 1093°C 2 hr Data provided by Carpenter Technology Corporation.Annealing followed by water quench and low stress grinding prior to tensile testing.Medical Implant Alloy. Non-magnetic Co-Cr-Mo alloy exhibiting h.. |
|||
Tensile Strength, Yield | 720 MPa @Temperature 550 °C |
104000 psi @Temperature 1020 °F |
R<sub>p</sub>02 |
Assab Steels 8407 2M Hot Work Steel ASSAB 8407 is a chromium-molybdenum-vanadium-alloyed steel which is characterized by: Good resistance to abrasion at both low and high temperatures. High level of toughness and ductility Uniform .. |
|||
Tensile Strength, Yield | 717 MPa @Strain 0.200 %, Temperature -73.3 °C |
104000 psi @Strain 0.200 %, Temperature -100 °F |
|
Carlson Nitronic® 33® Austenitic Stainless Steel General DescriptionNitronic 33 is a nitrogen-strengthened austenitic stainless steel that combines high yield strength with excellent toughness and ductility. It’s magnetic permeability remains v.. |
|||
Tensile Strength, Yield | 717 MPa @Strain 0.200 %, Temperature -73.0 °C |
104000 psi @Strain 0.200 %, Temperature -99.4 °F |
|
Carpenter Gall-Tough PLUS™ Stainless, Annealed, 10% Cold Work Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 r.. |
|||
Tensile Strength, Yield | 720 MPa @Temperature 550 °C |
104000 psi @Temperature 1020 °F |
R<sub>p</sub>02 |
Assab Steels 8407 SUPREME Hot Work Steel 8407 SUPREME is characterized by:High level of resistance to thermal shock and thermal fatigueGood high temperature strengthExcellent toughness and ductility in all directionsGood machinability and .. |