Carpenter Gall-Tough PLUS™ Stainless, Annealed, 10% Cold Work

Category	Metal , Ferrous Metal , Stainless Steel
Manufacturer	Carpenter Technology Corporation (Cartech)
Trade Name	Gall-Tough PLUS™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Carpenter Gall-Tough PLUS™ Stainless, Annealed, 10% Cold Work.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by Carpenter Technology Corporation.Annealed 1150°C, water quenched, and cold drawn.Threshold Galling Stress 48 MPa. The avg. total volume loss on the wear test is 10.6 mm³ at 100 rpm.Gall-Tough PLUS™ stainless is a high silicon, high manganese, nitrogen strengthened, austenitic stainless alloy which exhibits superior self-mated galling resistance and metal-to-metal wear resistance. The alloy possesses higher strength than Type 316. It also exhibits chloride corrosion resistance equal to or better then Type 316, along with equivalent high temperature oxidation resistance.Gall-Tough PLUS™ is a trademark of Carpenter Technology Corporation.

Physical Properties	Metric	English	Comments
Density	7.60 g/cc	0.275 lb/in³

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	827 MPa	120000 psi
	1144 MPa @Temperature -73.0 °C	165900 psi @Temperature -99.4 °F
Tensile Strength, Yield	544 MPa @Strain 0.200 %	78900 psi @Strain 0.200 %
	717 MPa @Strain 0.200 %, Temperature -73.0 °C	104000 psi @Strain 0.200 %, Temperature -99.4 °F
Elongation at Break	50 %	50 %	in 4D
	56 % @Temperature -73.0 °C	56 % @Temperature -99.4 °F	in 4D
Reduction of Area	70 %	70 %
	69 % @Temperature -73.0 °C	69 % @Temperature -99.4 °F
Modulus of Elasticity	184.9 GPa	26820 ksi

Thermal Properties	Metric	English	Comments
CTE, linear	14.19 µm/m-°C @Temperature 25.0 - 50.0 °C	7.883 µin/in-°F @Temperature 77.0 - 122 °F
	17.1 µm/m-°C @Temperature 25.0 - 250 °C	9.48 µin/in-°F @Temperature 77.0 - 482 °F
	18.07 µm/m-°C @Temperature 25.0 - 500 °C	10.04 µin/in-°F @Temperature 77.0 - 932 °F
Specific Heat Capacity	0.5055 J/g-°C @Temperature 50.0 - 100 °C	0.1208 BTU/lb-°F @Temperature 122 - 212 °F
Thermal Conductivity	12.0 W/m-K	83.3 BTU-in/hr-ft²-°F
Maximum Service Temperature, Air	982 °C	1800 °F	Scaling Temperature for Continuous Service

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.15 %	<= 0.15 %
Chromium, Cr	16.5 - 21 %	16.5 - 21 %
Iron, Fe	62 %	62 %	as remainder
Manganese, Mn	4.0 - 8.0 %	4.0 - 8.0 %
Molybdenum, Mo	0.50 - 2.5 %	0.50 - 2.5 %
Nickel, Ni	6.0 - 10 %	6.0 - 10 %
Nitrogen, N	0.050 - 0.35 %	0.050 - 0.35 %
Phosphorous, P	<= 0.040 %	<= 0.040 %
Silicon, Si	2.5 - 4.5 %	2.5 - 4.5 %
Sulfur, S	<= 0.040 %	<= 0.040 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.0000947 ohm-cm	0.0000947 ohm-cm