Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 690 MPa | >= 100000 psi | |
Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H925 (H925) Temper; All Sizes (UNS N03360) Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011. |
|||
Tensile Strength, Yield | >= 690 MPa | >= 100000 psi | 1/2 t |
Industeel SUPERELSO® 690CR Quenched and Tempered High Strength Steel for Leg Components of Jack-up Rigs Superelso® 690 CR (SE 690 CR) is a 690MPa (100ksi) yield strength quenched and tempered steel adapted for jack-up rig legs of offshore drilling platforms. Superelso® 690 CR is manufactured via.. |
|||
Tensile Strength, Yield | >= 690 MPa @Strain 0.200 % |
>= 100000 psi @Strain 0.200 % |
|
Industeel SUPRALSIM® 690 HLE Steel for Welded and Weight-Saving Structures Description: SUPRALSIM® 690 is general steel plate for structure enables to make weight savings thanks to a minimum yield strength of 690 N/mm². Thanks to its exceptional purity rate (very low.. |
|||
Tensile Strength, Yield | 690 MPa | 100000 psi | |
Latrobe Nitralloy® 135 Modified VAC-ARC, Up to 1.5 in Premium Nitriding Steel NITRALLOY 135 MODIFIED VAC-ARC steel is a low alloy nitriding grade with moderate hardenability. It has been designed to provide a high case hardness and to maintain its core strength during the nit.. |
|||
Tensile Strength, Yield | >= 690 MPa | >= 100000 psi | |
MetalTek IN® 713 UNS N07713 Centri-Vac Nickel Cobalt Based Alloy Information provided by MetalTek |
|||
Tensile Strength, Yield | 690 MPa @Strain 0.200 % |
100000 psi @Strain 0.200 % |
|
Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
Tensile Strength, Yield | 690 MPa @Strain 0.200 %, Temperature 550 °C |
100000 psi @Strain 0.200 %, Temperature 1020 °F |
Precipitation Hardened prior to test |
Special Metals NIMONIC® Alloy 90 A precipitation-hardenable nickel-chromium-cobalt alloy having high stress-rupture strength and creep resistance at temperatures to about 1700°F (920°C). The alloy also has good resistance to.. |
|||
Tensile Strength, Yield | >= 690 MPa | >= 100000 psi | |
SSAB Tunnplat Domex® 690XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. Gene.. |
|||
Tensile Strength, Yield | 690 MPa | 100000 psi | ISO 527 |
Styrolution Absolan® 2300 Sparkle SAN Absolac 2300 Sparkle is a good flow gradeInformation provided by Styrolution |
|||
Tensile Strength, Yield | >= 690 MPa | >= 100000 psi | |
TIMET TIMETAL® 3-2.5 Titanium Alloy (Ti-3Al-2.5V; ASTM Grade 9) Aged Cold Workable Medium Strength Alloy. UTS, TYS, and elongation data below are specific to aged material; other specific condition entries are also available in MatWeb.Features: Cold formable and we.. |
|||
Tensile Strength, Yield | 690 MPa | 100000 psi | |
Elgiloy® Co-Cr-Ni Alloy, Strip, 10% Cold Reduction The strength, elongation, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, fati.. |
|||
Tensile Strength, Yield | 690 MPa | 100000 psi | |
Elgiloy® Co-Cr-Ni Alloy, Wire, 10% Cold Reduction The strength, shear modulus, and hardness values are specific to this cold reduction treatment; other values below are typical of Elgiloy®.General Elgiloy® information: High strength, ductility, f.. |
|||
Tensile Strength, Yield | >= 690 MPa @Diameter <=100 mm |
>= 100000 psi @Diameter <=3.94 in |
Re. , un-machined |
Assab Steels 709M Machinery Steel ASSAB 709M is an alloyed machinery steel with high strength in small and medium sizes. As standard ASSAB 705M is supplied tough hardened requiring no further heat treatment. It can be oil hardened t.. |
|||
Tensile Strength, Yield | 690 MPa | 100000 psi | R<sub>e</sub>. 700°C tempering temperature. Quenching in oil ø 120. Testpiece hardened by oil quenching from 850°C. |
Assab Steels 705M Machinery Steel ASSAB 705M is an alloyed machinery steel with good hardenability also in heavier sizes. As standard ASSAB 705M is supplied tough hardened with no further heat treatment required. It can be oil harde.. |
|||
Tensile Strength, Yield | 690 MPa | 100000 psi | |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304, 20% Cold Rolled (UNS S30400) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
Tensile Strength, Yield | 690 MPa | 100000 psi | |
ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 304L, 20% Cold Rolled (UNS S30403) This alloy is one of the most familiar and most frequently used alloy in the stainless steel family. It may be best used in applications where the following properties are important: resistance to .. |
|||
Tensile Strength, Yield | 690 MPa @Treatment Temp. 760 °C, Time 2.88e+7 sec |
100000 psi @Treatment Temp. 1400 °F, Time 8000 hour |
0.2%. Room temp test after thermal exposure |
Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-b.. |