Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 72 hours @ 150°C; ASTM D412 |
Precision Polymer Engineering H50B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 45-55 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. ASTM and ISO designation = GECO.Applications: Excellent resistance t.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 72 hours @ 150°C; ASTM D412 |
Precision Polymer Engineering H60B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 55-65 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. To ASTM D2000 line call-out: M3CH608, A25, B14, EO16, EO36, F17. AS.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
Precision Polymer Engineering S60A Silicone Rubber Blue Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Fe.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 225°C; ASTM D412 |
Precision Polymer Engineering S60Y Silicone Rubber Yellow Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States .. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 225°C; ASTM D412 |
Precision Polymer Engineering S60Z Silicone Rubber Grey Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Fo.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
Precision Polymer Engineering S70A Silicone Rubber Blue Silicone Rubber, 66-75 °IRHD.Complies with the formulation guidelines of the FDA. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain.Applications: Excellent .. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
Precision Polymer Engineering S70G Silicone Rubber Green Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States F.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | -25% change after 70 hours @ 200°C; ASTM D412 |
Precision Polymer Engineering S72R Silicone Rubber Orange Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States .. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
Petroquimica Triunfo Tritheva® TN 2007 EVA Copolymer The Tritheva TN 2007 resin is an Ethylene-Vinyl Acetate copolymer (EVA), developed to meet the multi-layer packaging needs where are required high strength, with high toughness, and excellent optica.. |
|||
Tensile Strength, Yield | 6.00 - 170 MPa | 870 - 24700 psi | Average value: 105 MPa Grade Count:16 |
Overview of materials for Nylon 6, Glass Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass Filled, Impact Grade". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | 70°C for 1,000 hrs; JIS-K-6251 |
Fujipoly Industries Sarcon® 25G-Td Thin-Film GR-TD Sarcon 25G-Td is a highly conformable, thermally conductive material in areas where space between surfaces is uneven and surface textures vary.Information provided by Fujipoly Industries |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | 150°C for 1,000 hrs |
Fujipoly Industries Sarcon® 30T Thin-Film TR Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of .. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | 200°C for 1,000 hrs |
Fujipoly Industries Sarcon® 85U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
LyondellBasell Adflexâ„¢ KS-084P TPO Resin Primary Processing Method: ExtrusionKey Features: high melt flow, low modulus, impact resistant thermoplastic olefin, resin, good heat sealability, outstanding puncture resistance, excellent balance.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
A. Schulman POLYFORT™ PX 1040 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
A. Schulman POLYFORT™ PX 1040 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | |
Trelleborg Commercial Neoprene® C800 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
Tensile Strength, Yield | 6.00 MPa @Strain 50.0 % |
870 psi @Strain 50.0 % |
50 mm/min |
Arkema Group Nakan® FKS 911 S PVC, Soft Extrusion Grade NAKAN FKS 911 S is a soft polyvinyl chloride compound developed for high speed insulation.ISO data provided by the manufacturer, Arkema. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | |
BASF Lucalen® A 2910 M Q 47 Ethylene/Acrylate Copolymer Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | |
BASF Lucalen® A 2920 M Ethylene/Acrylate Copolymer Used in the manufacture of economical composite films of Lucalen and PE-LD, and as a primer for aluminum steel composites.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | 50 mm/min |
Arkema Group Evatane® 1003 VL 4S Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Anti-UV stabilized grade. Applications Grade for transparent and thermal agricultural film to 180 at 200 µ for greenhouse coverage.ISO data prov.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | 50 mm/min |
Arkema Group Evatane® 1003 VN 4 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for transparent and thermal agricultural film for greenhouse coverage.ISO data provided by the manufacturer, Arkema. |
|||
Tensile Strength, Yield | 6.00 MPa @Strain 50.0 % |
870 psi @Strain 50.0 % |
50 mm/min |
Arkema Group Nakan® FEM 781 N PVC, Soft Extrusion Grade NAKAN FEM 781 N is a soft polyvinyl chloride compound developed for extrusion of tubes for perfusion, pouches for solutions and blood.ISO data provided by the manufacturer, Arkema. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | Film Property, 50 µm thickness; ASTM D882 |
Arkema Group OREVAC® 9309 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength, Yield | 6.00 MPa @Strain 100 % |
870 psi @Strain 100 % |
ASTM D-412 |
BASF Elastollan® C85A10 (917) Wire & Cable Grade Polyurethane Elastomer As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | |
Trelleborg Commercial Neoprene® C803 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade.. |
|||
Tensile Strength, Yield | 6.00 MPa @Strain 50.0 % |
870 psi @Strain 50.0 % |
50 mm/min |
Arkema Group Nakan® FKC 911 S PVC, Soft Extrusion Grade NAKAN FKC 911 S is a soft polyvinyl chloride compound developed for L.S.F. insulation and sheeting - BS 5467.ISO data provided by the manufacturer, Arkema. |
|||
Tensile Strength, Yield | 6.00 MPa | 870 psi | ASTM D638 |
A. Schulman POLYFORT™ PX 1040 Information provided by A. Schulman. |