Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 %, Temperature 760 °C |
66700 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Tensile Strength, Yield | 460 MPa | 66700 psi | Annealed |
Special Metals INCONEL® Alloy 625 Niobium content includes tantalum. A nickel-chromium-molybdenum alloy with an addition of niobium that acts with the molybdenum to stiffen the alloy's matrix and thereby provide high strength witho.. |
|||
Tensile Strength, Yield | >= 460 MPa | >= 66700 psi | |
SSAB Tunnplat Domex® 460MC HSLA Steel HSLA SteelCharacteristics: Some thicknesses of these steel grades are available with a maximum of 0.03% Si for thin Zn coating. If the material is to be hot-dip galvanized and steel with a maximum .. |
|||
Tensile Strength, Yield | >= 460 MPa @Strain 0.200 % |
>= 66700 psi @Strain 0.200 % |
|
Schmolz + Bickenbach UGICHROM 4460 Duplex Chrome Plated Bar Description: Ugichrom combines the high efficiency of micro-fissuring chromium plating with the technology of Ugitech’s most advanced gradesAdvantages: Zero defects guarantee; Low friction coef.. |
|||
Tensile Strength, Yield | >= 460 MPa | >= 66700 psi | 35<x=60mm |
ThyssenKrupp XABO® 500 T Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
Typical |
TIMET TIMETAL® Code 12 Titanium Alloy (ASTM Grade 12) Features: Highly weldable, near-alpha alloy, exhibiting improved strength and temperature capability over CP combined with superior crevice corrosion resistance and excellent resistance under oxidiz.. |
|||
Tensile Strength, Yield | >= 460 MPa | >= 66700 psi | |
ThyssenKrupp PAS 460 Structural Steel for Cold Forming This Material Specification applies to plates made of low carbon high strength steels with minimum yield strength values between 315 and 700 MPa1) in the thermo mechanically rolled delivery conditio.. |
|||
Tensile Strength, Yield | >= 460 MPa | >= 66700 psi | 35<x=60mm |
ThyssenKrupp XABO® 500 Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |
|||
Tensile Strength, Yield | 460 - 550 MPa | 66700 - 79800 psi | |
ArcelorMittal HSLA 460 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S460MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |
|||
Tensile Strength, Yield | 460 - 550 MPa | 66700 - 79800 psi | |
ArcelorMittal TRIP 780 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT780T), electrogalvanized (HCT780T+ZE) and Extragal®/Galvannealed (HCT780T+Z/+ZZF)Description: TRIP steels offer an outstanding combination of strength and d.. |
|||
Tensile Strength, Yield | >= 460 MPa @Thickness 35.0 mm |
>= 66700 psi @Thickness 1.38 in |
|
ThyssenKrupp XABO® 460 Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |
|||
Tensile Strength, Yield | 460 MPa @Strain 0.200 % |
66700 psi @Strain 0.200 % |
|
Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
Tensile Strength, Yield | >= 460 MPa @Thickness 35.0 mm |
>= 66700 psi @Thickness 1.38 in |
|
ThyssenKrupp XABO® 460 T Structural Steel This Material Specification applies to thermo mechanically rolled flat products in thicknesses up to 60 mm. The criteria to distinguish the steel grades is the lowest test temperature for the notch-.. |