Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 35.9 MPa | 5210 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne LubriOne™ ATT-000/5T Black Acetal (POM) Copolymer LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | 2 in per min; ASTM D638 |
Network Polymers NPP 30-1200 A Description: Homopolymer Polypropylene Nucleated with AntistaticInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Network Polymers Nylon 6040 Description: Natural NylonInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Polymer Resources ABS-FR1 ABS, Flame Retardant Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Polymer Resources ABS-GP1-[color]-3 ABS, General Purpose, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Tensile Strength, Yield | 35.9 MPa @Thickness 3.20 mm |
5200 psi @Thickness 0.126 in |
At 51mm/min, injection molded ASTM Type 1 specimen; ASTM D638 |
Pinnacle Polymers 1703 Polypropylene Homopolymer, Stretched Tape Grade This Pinnacle Polymers Polypropylene is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties an.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N339 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 75A MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5210 psi | |
Ineos ABS Centrex® 813 ASA+AES Blend
(discontinued **) Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingInformation provided by Ba.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Fiberfil® PP-60/TC/10 Polypropylene Homopolymer, 10% Talc Filled Information provided by FIBERFIL Engineered Plastics |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Fiberfil® PP-60/VO Polypropylene Homopolymer, Flame Retardant, UL94 V0 Information provided by FIBERFIL Engineered Plastics |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | 2 in/min; ASTM D638 |
Ineos H12G-01 Polypropylene Homopolymer Grade H12G-01 is a general purpose homopolymer. This material meets the requirements of the US Food and Drug Administration as specified in 21 CFR 177.1520 for use in food-contact applications for f.. |
|||
Tensile Strength, Yield | 35.9 - 51.7 MPa | 5200 - 7500 psi | ASTM D638 |
Techmer ES Elastoblend® PA6 IM 435 HS L Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedUses: Low Temperature ApplicationsInformatio.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Spartech Royalite R26 ABS General Purpose Sheet Description: General Purpose SheetInformation provided by Spartech. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Spartech Royalite R59 ABS/PVC Fire Rated Sheet Description: Fire Rated SheetInformation provided by Spartech. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Westlake Plastics Kynar® PVDF CN-P Polyvinylidene Fluoride (conductive) Carbon-powder-filled, thermally stable, conductive material with consistent resistivities |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | 2" (50mm) per min.; ASTM D638 |
Formosa Plastics Formolene® 5100J Blown and Cast Film Polypropylene HomopolymerApplications: Cast and blown film applications.Formolene 5100J is a high molecular weight, highly isotactic polypropylene homopolymer designed for sheet, cast and blown film applications... |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 75A MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N339 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Engineered Polymer Solutions ABS 450 Low Gloss, Medium Impact. Natural and colors available. Injection molding grade. Uses: General PurposeInformation provided by Engineered Polymer Solutions. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | chs 2 in/min; ASTM D638 |
Diamond Polymers ASA S950 Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D412 |
Clariant Renol TPU2087AFR Polyurethane Elastomer, Flame Retardant Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | 35.9 MPa | 5210 psi | 2 in/min (50 mm/min); ASTM D638 |
Bapolene® 4012 Polypropylene, Extrusion Grade Bapolene PP4012 is a general purpose extrusion resin with excellent stiffness and processability, chemical resistance, and ESCR properties. This product meets FDA standards for food contact applic.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5210 psi | 2 in/min (50 mm/min); ASTM D638 |
Bapolene® 4082 Polypropylene, Injection Grade Bapolene PP4082 is a high flow, fast cycle injection molding resin. Injection molded parts exhibit good stiffness and chemical resistance. This product meets FDA standards for food contact applica.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | ASTM D638 |
Plastics Group Polifil® RP-ABS Acrylonitrile-Butadiene Styrene, High Flow Version Polifil® RP- Acrylonitrile-Butadiene Styrene is a styrenic resin with improved toughness and heat resistance versus HIPS grades. ABS exhibits high gloss, low shrinkage, and good dimensional stabili.. |
|||
Tensile Strength, Yield | 35.9 MPa @Temperature 23.0 °C |
5200 psi @Temperature 73.4 °F |
ASTM D638 |
Ineos H20G-00 Polypropylene Homopolymer This is a general purpose homopolymer for injection molding applications. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.ApplicationsC.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5200 psi | 2.0 in/min; ASTM D638 |
LTL Color Compounds ColorFast® GPA300X ABS Extrusion grade, high impact, high gloss ABSAll information provided by LTL Color Compounders, Inc. |
|||
Tensile Strength, Yield | 35.9 MPa | 5210 psi | ASTM D638 |
Eastman Tenite Butyrate 465E2R30008 Natural, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 8%. Weight loss on heating = 0.7% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
Tensile Strength, Yield | 35.9 MPa | 5210 psi | ASTM D638 |
Eastman Tenite Butyrate 513E3720012 Clear, Trsp Cellulose Acetate Butyrate