Polymer Property : Tensile Strength, Yield = 3.70 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	3.70 MPa	536 psi	at 200%, post cured- 2 hours at 177°C
Multibase SILASTIC® Q7-4765 Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase
Tensile Strength, Yield	3.70 MPa	537 psi	ASTM D412
Polymax® Maxelast® A9740 TPE, ABS/PC Overmold Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesInform..
Tensile Strength, Yield	3.70 MPa	537 psi	M100
3M Dyneon™ Fluorel™ FC-2123 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Excellent hot tear and compression se..
Tensile Strength, Yield	3.70 MPa	537 psi	M100
3M Dyneon™ Fluorel™ FT-2350 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 68.6%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Improved retention of elongation afte..
Tensile Strength, Yield	>= 3.70 MPa	>= 536 psi	Stress at Elongation M100; ASTM D412 Method A
Seals Eastern 5484 Nitrile Rubber Low temperature service NitrileInformation provided by Seals Eastern, Inc.
Tensile Strength, Yield	3.70 MPa @Strain 100 %	537 psi @Strain 100 %
Daikin DAI-EL G-603 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 71% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Information provided by Daikin Industries.
Tensile Strength, Yield	3.70 MPa @Strain 100 %	537 psi @Strain 100 %
Daikin DAI-EL G-621 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 71% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: General purpose with excellent sol..
Tensile Strength, Yield	3.70 MPa @Strain 50.0 %	537 psi @Strain 50.0 %	50 mm/min
Arkema Group Pebax® 3533 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 35 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness..