3M Dyneon™ Fluorel™ FC-2123 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)

Category	Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ Fluorel™ FC-2123 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Excellent hot tear and compression set. Good metal adhesion. Suggested alternative: FE-5622Q Used in Molded Goods Applications.

Physical Properties	Metric	English	Comments
Density	1.80 g/cc	0.0650 lb/in³
Oxygen Transmission	98.0 cc-mm/m²-24hr-atm	249 cc-mil/100 in²-24hr-atm
Mooney Viscosity	25 @Temperature 121 °C	25 @Temperature 250 °F	ML1+10

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	71	71
Tensile Strength, Ultimate	16.0 MPa	2320 psi
Tensile Strength, Yield	3.70 MPa	537 psi	M100
Elongation at Break	270 %	270 %
Coefficient of Friction, Dynamic	0.80	0.80
Compression Set	20 % @Temperature 200 °C	20 % @Temperature 392 °F	70 hr; ASTM D395B

Thermal Properties	Metric	English	Comments
CTE, linear	200 µm/m-°C @Temperature 20.0 °C	111 µin/in-°F @Temperature 68.0 °F
Specific Heat Capacity	1.65 J/g-°C	0.394 BTU/lb-°F
Thermal Conductivity	0.240 W/m-K	1.67 BTU-in/hr-ft²-°F
Glass Transition Temp, Tg	-18.0 °C	-0.400 °F	TR10

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+13 - 1.00e+14 ohm-cm	1.00e+13 - 1.00e+14 ohm-cm
Dielectric Constant	11.4 @Frequency 6.00e+7 Hz	11.4 @Frequency 6.00e+7 Hz
Dielectric Strength	25.0 kV/mm	635 kV/in