Daikin DAI-EL G-621 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 71% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-621 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 71% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Features: General purpose with excellent solvent resistance.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.92 g/cc
1.92 g/cc
at 25°C
Mooney Viscosity 50

@Temperature 121 °C
50

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 76
76
Peak value, at 25°C
Tensile Strength at Break 16.2 MPa
2350 psi
Tensile Strength, Yield 3.70 MPa

@Strain 100 %
537 psi

@Strain 100 %
Elongation at Break 280 %
280 %
Tear Strength 19.6 kN/m
112 pli
at 25°C
Compression Set 23 %
23 %
70 hours at 25°C
18 %

@Temperature 100 °C
18 %

@Temperature 212 °F
70 hours
20 %

@Temperature 175 °C
20 %

@Temperature 347 °F
70 hours
29 %

@Temperature 200 °C
29 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -8.00 °C
17.6 °F
TR test, TR10
-5.00 °C
23.0 °F
Gehman torsion test, T10
-2.00 °C
28.4 °F
TR test, TR70
-1.50 °C
29.3 °F
Gehman torsion test, T2
Brittleness Temperature -15.0 °C
5.00 °F
Processing Properties Metric English Comments
Processing Temperature 170 °C
338 °F
Cure Measuring Temperature
Cure Time 3.50 min
0.0583 hour
Curelastmeter