Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PP 1373 PRE-ELEC PP 1373 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELE.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
Reliance Industries Relene B56003 Polyethylene Relene B56003 is a High Density Polyethylene grade suitable for general purpose extrusion blow molding applications. Articles blown from this grade exhibit good stiffness. The resin offers good me.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527-2 |
Total Lacqrene® 3351(EU) Impact Polystyrene
(discontinued **) LACQRENE® 3351 is a high heat resistance, high impact polystyrene for injection molding and extrusion/thermoforming. It is recommended for the manufacture of articles which require good dimensiona.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527-2 |
Total Lacqrene® 4241 High Impact Polystyrene
(discontinued **) DescriptionLACQRENE® 14240 is a high heat resistance, high impact polystyrene for the extrusion industry. Good mechanical and thermal properties leads to the production of thermoformed articles of.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
BP Amoco Acctuf® 3243 Impact Copolymer Polypropylene
(discontinued **) Suggested fabrication methods: Injection moldingFeatures: General purposeComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection molded samples. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638M |
DSM Somos® 8120 Epoxy Photopolymer
(discontinued **) DescriptionDSM Somos® 8120 is a high-speed liquid photopolymer that produces flexible, high-impact-strength, accurate parts using stereolithography machines. It has a wide processing latitude and .. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in per min; ASTM D638; Test specimens were injection molded by ASTM D1897. |
Chevron Phillips K-Resin® KR99HG Styrene-Butadiene Copolymer, Injection Molding Grade
(discontinued **) Styrene-Butadiene CopolymerCustomer Benefits: This SBC is easily processed by injection molding. Molded parts provide excellent part detail on fast production cycles. Molded parts have excellent c.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
LyondellBasell Lupolen® 5261 ZS HDPE, Blow Molding Grade Relatively high viscosity blow molding grade (similar to Lupolen 5261 Z), but more resistant to stress cracking) for rigid, stackable and highly shock resistant containers for packaging all types of.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
Flint Hills AP6106-HS Impact Copolymer Polypropylene High impact copolymer, UL certified, and FDA compliant. Features: Heat stabilizedApplications: Injection molding: child protection systems, appliance components, consumer durables, and automotive in.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
Flint Hills P6G4Z-097 Impact Copolymer Polypropylene Features: Good impact/stiffness balance. Product does not contain animal derived components.Applications: Injection Molding - appliance components, consumer durables, caps and closures.Informatio.. |
|||
Tensile Strength, Yield | 26.0 MPa @Temperature 23.0 °C |
3770 psi @Temperature 73.4 °F |
ISO 527-2/50 |
MBA Polymers PS 3122 Post-consumer recycled impact modified polystyrene Available in standard black.Information provided by MBA Polymers. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
LyondellBasell Astryn 75F4-2 Polypropylene Copolymer, 20% Talc Key Features: conventional melt flow, medium high modulus, mineral-filled polypropylene copolymer, excellent impact and stiffness balance, good colorability, good aestheticsApplications: small appli.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50mm/min; ISO 527-2 |
Borealis MG9621B Polyethylene Applications: crates, and pailsInformation provided by Borealis AG |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 3452 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 3452 is a 30% mineral filled copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527 |
Unipetrol PP MONSTEN® MA 745 Polypropylene Impact Copolymer Made for injection molding applications. Antistatic stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product DescriptionPolyfort® CFP 4611 is an 11% CACO3 filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50 mm/min; ASTM D638 |
A. Schulman PP 1930-01 Polypropylene Copolymer Polypropylene DescriptionPolypropylene PP 1930-01 is an automotive recognized copolymer polypropylene for use on interior trim applications.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
Total PSI 8350 (AS) High Impact Polystyrene Total Petrochemicals Polystyrene 8350 (AS) is a very high impact polystyrene for extrusion and injection molding. This grade has improved environmental stress crack resistance in comparison with st.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 3045 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product DescriptionPolyfort® CFP 4611 is an 11% CACO3 filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527 |
Unipetrol PP MONSTEN® MT 802 Polypropylene Random Copolymer Applications include injection molding and extrusion. Antistatic and transparent stabilization. Random copolymer.Information provided by Unipetrol RPA |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in/min; Type IV bar; ASTM D638 |
Chevron Phillips Marlex® 9505H High Density Polyethylene This gas phase, high molecular weight, hexene copolymer with antistatic agent is tailored for lightweight blow molded containers that:Require outstanding ESCRRequire excellent impact resistanceAre d.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ CNU 015 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with good stiffness/toughness balance, low odor and emissions, designed for automotive interior applications. Availability: Africa & M.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
Braskem CP 741 Blow Molding Polypropylene Description: CP 741 is a low melt flow rate heterophasic copolymer. It has broad molecular weight distribution and general purpose additive package. CP 741 presents low odor/taste transfer, high mel.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
Aclo Accutech Polypropylene CP0405UVV Copolymer UV Stabilized Approved to Suzuki PP-S2 Med Grey T01 |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
Addcomp PRIEX® Ionomer 30101 HDPE Ionomers will be used toStrengthen rigidity and hardness while maintaining impact resistance in polyolefinsMaintain adhesion even under contaminated conditions especially in fatty substratesReduce t.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
BASF Procom® D 1133 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | XY direction; ASTM D638 |
ALM FR 106 Nylon 11 SLS Prototyping Polymer This flame retardant rapid prototyping material has additives in the raw material that allows it to pass aeronautic standard FAR25.853 smoke, flame, and toxicity tests. This material is ideal for Ae.. |
|||
Tensile Strength, Yield | 26.0 MPa | 3770 psi | 2 in/min; ASTM D638 |
A. Schulman POLYPUR™ FPU 1152C Thermoplastic Polyurethane Information provided by A. Schulman. |