Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 400 MPa @Strain 1.00 % |
58000 psi @Strain 1.00 % |
Outokumpu Typical,Hot rolled Strip/Sheet (CPP); EN 10002-1 |
Outokumpu 353MA® High Temperature Austenitic Stainless Steel Alloy with higher nickel content than the other steels. Has increased silicon and nitrogen contents and is microalloyed with rare earth metals (REM). Max service temperature in air is 1150°C, but.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 %, Temperature 200 °C |
58000 psi @Strain 0.200 %, Temperature 392 °F |
EN min.; EN 10002-5 |
Outokumpu 4021 Martensitic Stainless Steel Moderate corrosion resistant stainless steel hardenable up to 1000N/mm2. Re-sulphurized steel improves machining properties.Applications: ShaftsKnivesFastenersSurgical applicationsDomestic applicat.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 1.00 %, Temperature -196 °C |
58000 psi @Strain 1.00 %, Temperature -321 °F |
EN min.; EN 10002-5 |
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 1.00 %, Temperature -196 °C |
58000 psi @Strain 1.00 %, Temperature -321 °F |
EN min.; EN 10002-5 |
Outokumpu 4307 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 %, Temperature 200 °C |
58000 psi @Strain 0.200 %, Temperature 392 °F |
EN min.; EN 10002-5 |
Outokumpu 4501 Duplex Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form. |
|||
Tensile Strength, Yield | 400 MPa @Strain 1.00 %, Temperature 100 °C |
58000 psi @Strain 1.00 %, Temperature 212 °F |
EN min.; EN 10002-5 |
Outokumpu 4565 High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
EN min.,RT; EN 10002-1 |
Outokumpu SAF 2304® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 %, Temperature 200 °C |
58000 psi @Strain 0.200 %, Temperature 392 °F |
EN min.; EN 10002-5 |
Outokumpu SAF 2507® Duplex Stainless Steel Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical tankersSeawater systemsFirewalls and blast walls on offshore platformsBridgesCompone.. |
|||
Tensile Strength, Yield | 400 MPa @Thickness 3.17 mm |
58000 psi @Thickness 0.125 in |
CW |
Industrial Laminates/Norplex NP180 Synthetic Fabric
(discontinued **) Description: aramid fabric material with a high performance epoxy resin matrix. Excellent electrical and mechanical properties at elevated temperatures and in adverse environments.Thickness Tested: .. |
|||
Tensile Strength, Yield | >= 400 MPa @Strain 0.200 % |
>= 58000 psi @Strain 0.200 % |
|
Industeel URANUS® 35N 23.04 Duplex Stainless Steel with PREN = 24 Description: URANUS® 35N (UR 35N) is a 23% Cr, 4% Nickel, Mo free duplex stainless steel (23.04). The alloy UR 35N has similar corrosion resistance properties similar to 316L. Furthermore, its me.. |
|||
Tensile Strength, Yield | 400 MPa @Thickness 12.7 mm, Temperature 149 °C |
58000 psi @Thickness 0.500 in, Temperature 300 °F |
0.2% Offset |
Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate HASTELLOY® HYBRID-BC1® alloy possesses much higher resistance to hydrochloric and sulfuric acids than the nickel-chromium-molybdenum (C-type) alloys, and can tolerate the presence of oxidizing.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
after porcelain firing |
Wieland Porta Aurium PFM Alloy All-purpose alloy for low-fusing high expanding ceramicsApplications: inlays/onlays, crowns, short span bridges, long span bridges, telescopic and milling works, removable partials, ceramic veneerin.. |
|||
Tensile Strength, Yield | 400 MPa @Temperature 177 °C |
58000 psi @Temperature 351 °F |
|
Hexcel® F161 Epoxy Resin, 120 Glass Fabric Hexcel designation: 120-38"-F161; Fiber: 450-1/2Information provided by HexCel |
|||
Tensile Strength, Yield | 400 MPa @Temperature 71.0 °C |
58000 psi @Temperature 160 °F |
|
Hexcel® HexPly® F155 Epoxy Resin, K120 Kevlar Fabric Fiber: Kev. 49 195Information provided by HexCel |
|||
Tensile Strength, Yield | 400 MPa @Temperature 80.0 °C |
58000 psi @Temperature 176 °F |
Warp TS |
Hexcel® HexPly® M26/M26T 120°C (250°F) Curing Epoxy Matrix, M26T/50%/7581 Glass Fabric 300 gsmInformation provided by HexCel |
|||
Tensile Strength, Yield | >= 400 MPa @Strain 0.200 %, Thickness 100 - 140 mm |
>= 58000 psi @Strain 0.200 %, Thickness 3.94 - 5.51 in |
Temper T651 |
Constellium Certal® Thick Aluminum Plate Certal® thick plates have been optimized to provide excellent machinability, shape stability and high strength. Certal® is therefore ideal for industrial tools. Applications include injection and .. |
|||
Tensile Strength, Yield | >= 400 MPa @Strain 0.200 %, Thickness 140 - 160 mm |
>= 58000 psi @Strain 0.200 %, Thickness 5.51 - 6.30 in |
|
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
As-Consolidated |
Crucible Compaction Metals P/M 625 Corrosion Resistant Alloy P/M 625 (chemically, UNS N06625) is produced by the Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing (HIP) and/or extrusion. The Crucible powder con.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
As-Extruded |
Crucible Compaction Metals P/M 625M Corrosion Resistant Alloy P/M 625M (chemically, UNS N07626) is produced by the state-of-the-art Crucible P/M process: inert gas atomization, coupled with consolidation by hot isostatic pressing (HIP) and/or extrusion. The a.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
Carburized |
Carlson Nitronic® 60® Austenitic Stainless Steel General DescriptionNitronic 60 is an anti-galling and wear resistant austenitic stainless steel. It provides a significantly lower cost alternative to combat wear and galling when compared with cob.. |
|||
Tensile Strength, Yield | >= 400 MPa @Strain 0.200 % |
>= 58000 psi @Strain 0.200 % |
Minimum |
Aleris Hokotol Aluminum Alloy, 300 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an.. |
|||
Tensile Strength, Yield | 400 MPa @Strain 0.200 % |
58000 psi @Strain 0.200 % |
Annealed 1052°C |
Latrobe MP159® Alloy MP159 is an alloy of the Multiphase family of alloys possessing the unique combination of ultra-high strength, ductility and corrosion resistance. Through work strengthening and aging, MP159 alloy .. |