Outokumpu 4565 High Performance Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Pressure Vessel Steel , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 4565 High Performance Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quarto) form.
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
RT
Mechanical Properties Metric English Comments
Hardness, Brinell >= 240
>= 240
Hot rolled plate/Hot rolled strip/Cold rolled strip; EN 10003-1
Tensile Strength, Ultimate 825 MPa
120000 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
610 MPa

@Temperature 400 °C
 88500 psi

@Temperature 752 °F
 EN min.; EN 10002-5
640 MPa

@Temperature 200 °C
 92800 psi

@Temperature 392 °F
 EN min.; EN 10002-5
640 MPa

@Temperature 300 °C
 92800 psi

@Temperature 572 °F
 EN min.; EN 10002-5
750 MPa

@Temperature 100 °C
 109000 psi

@Temperature 212 °F
 EN min.; EN 10002-5
Tensile Strength, Yield 420 MPa

@Strain 0.200 %
 60900 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
440 MPa

@Strain 0.200 %
 63800 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
480 MPa

@Strain 1.00 %
 69600 psi

@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
210 MPa

@Strain 0.200 %,
Temperature 400 °C
 30500 psi

@Strain 0.200 %,
Temperature 752 °F
 EN min.; EN 10002-5
240 MPa

@Strain 0.200 %,
Temperature 300 °C
 34800 psi

@Strain 0.200 %,
Temperature 572 °F
 EN min.; EN 10002-5
240 MPa

@Strain 1.00 %,
Temperature 400 °C
 34800 psi

@Strain 1.00 %,
Temperature 752 °F
 EN min.; EN 10002-5
270 MPa

@Strain 1.00 %,
Temperature 300 °C
 39200 psi

@Strain 1.00 %,
Temperature 572 °F
 EN min.; EN 10002-5
270 MPa

@Strain 0.200 %,
Temperature 200 °C
 39200 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
310 MPa

@Strain 1.00 %,
Temperature 200 °C
 45000 psi

@Strain 1.00 %,
Temperature 392 °F
 EN min.; EN 10002-5
350 MPa

@Strain 0.200 %,
Temperature 100 °C
 50800 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
400 MPa

@Strain 1.00 %,
Temperature 100 °C
 58000 psi

@Strain 1.00 %,
Temperature 212 °F
 EN min.; EN 10002-5
Elongation at Break 55 %
55 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Modulus of Elasticity 190 GPa
27600 ksi
RT
165 GPa

@Temperature 400 °C
 23900 ksi

@Temperature 752 °F
Impact Test >= 90.0 J
>= 66.4 ft-lb
Hot rolled plate/Hot rolled strip/Cold rolled strip; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 14.5 µm/m-°C

@Temperature 100 °C
 8.06 µin/in-°F

@Temperature 212 °F
16.8 µm/m-°C

@Temperature 400 °C
 9.33 µin/in-°F

@Temperature 752 °F
Specific Heat Capacity 0.450 J/g-°C
0.108 BTU/lb-°F
RT
Thermal Conductivity 12.0 W/m-K
83.3 BTU-in/hr-ft²-°F
RT
18.0 W/m-K

@Temperature 400 °C
 125 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.020 %
0.020 %
Chromium, Cr 24 %
24 %
Iron, Fe 48.53 %
48.53 %
Manganese, Mn 5.5 %
5.5 %
Molybdenum, Mo 4.5 %
4.5 %
Nickel, Ni 17 %
17 %
Nitrogen, N 0.45 %
0.45 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000920 ohm-cm
0.0000920 ohm-cm
RT
Processing Properties Metric English Comments
Annealing Temperature 1120 - 1170 °C
2050 - 2140 °F
Solution Annealing