Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 48.3 MPa | 7000 psi | 2 in/min; ASTM D638 |
RheTech Products GC20P255-01UV 20% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, UV Stabilized, Black Applications: Durable goodsStructural componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources PPX-GP3-WR Modified-PPO, Wear Resistant Modified-Polyphenylene Oxide, Wear Resistant, 235F HDTFeatures: • Hydrolytically Stable • Low to No Water Absorption • Good Wear ResistanceProcess: Injection MoldingNotes: All physical, mechan.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources TP-GP2 Polybutylene Terephthalate, General Purpose Polybutylene Terephthalate, General Purpose Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provid.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Polymer Resources TP-M30 Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced Warpage Polybutylene Terephthalate, 30% Mineral Reinforced, Reduced WarpageProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Ravago Manufacturing Americas Hysun™ 678UV ASA Available in North America Additive: UV Stabilizer Features: Good Impact Resistance and High Heat ResistanceRoHS CompliantForm: PelletsInformation provided by Ravago |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Techmer ES Plaslube® PC-50/TF/13/SI/2 NAT Polycarbonate |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | non-oriented film; ASTM D882 |
Total PPR 6575 Polypropylene, Random Copolymer, Film Grade Color. Low catalyst residuals in TOTAL Petrochemicals 6575 polypropylene results in improved color stability.Clarity/Impact. The random copolymer structure of 6575 improves its clarity and resilien.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | TM R050-36 |
Resinlab® EP11HTFS Gray Filled Epoxy Adhesive Resinlab™ EP11HTFS Gray is a two part filled epoxy adhesive designed for bonding metals and plastics. It cures at room temperature to a tough, semi-rigid material. It has good wetting to most surfa.. |
|||
Tensile Strength at Break | 48.3 MPa | 7000 psi | ASTM D638 |
Chase Plastics CP Pryme® PCA300 General Purpose Polycarbonate/ABS Alloy (Utility Grade) Information provided by Chase Plastics. |