Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 25.5 MPa | 3700 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable EAC31L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products HP517-00 23% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Interior trim moldingsSill platesTire coverInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products P258-01 Polypropylene Copolymer, UV Stabilized, Black Applications: Door/trunk scuffExterior grills and cowlsSteering column shroudsInterior trimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products P261-01 Polypropylene Copolymer, Medium Impact, Black Applications: Radiator grille inlet supportElectrical housingsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products UVP254-01 Polypropylene Copolymer, UV Stabilized, Black Applications: Fuel filler pocketInterior trimI/P componentsCenter consoleInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | chs 2 in/min; ASTM D638 |
Network Polymers MS 175 Styrene Methyl Methacrylate Terpolymer Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Niche Polymer PPCT40BK Copolymer PP, 40% Talc Filled Information provided by Niche Polymer |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 2 in/min; ASTM D638 |
RheTech Products HP512-01 High Stiffness Polypropylene Copolymer, UV Stabilized, Black Applications: Automotive interior applicationsSeat back trimCenter consolesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 25.5 MPa @Thickness 2.00 mm |
3700 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
LG Chemical KEYFLEX BT 1140D Ester Type TPE Description: Injection Molding, TPC-ET, General Purpose, Medium ModulusApplication: Cable & Wire Jackets, Hose & Tubing, SheetCAS: 37282-12-5Information provided by LG Chemical |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D412 |
Huntsman IROGRAN® A 60 E 4612 N TPU-Polyester Performance Features: Manufactures of technical parts can achieve the highest levels of: Wear and tear strengthDimensional stabilityOil resistanceLow compression setDynamic load performanceElasticit.. |
|||
Tensile Strength at Break | >= 25.5 MPa | >= 3700 psi | |
Sibur Nitrilast-40 Nitrile-Butadiene Rubber (NBR) N 3883. For production of oil-benzene resistant articles for the automobile, aviation and rubber technical industries. Rubbers on the base of Nitrilast possess good oil-benzene resistance. Rubber.. |
|||
Tensile Strength at Break | >= 25.5 MPa | >= 3700 psi | |
Sibur SKS-30 ARK 2nd Grade Styrene-Butadiene Rubber (SBR) SBR-1500. For use in the shoe industry and for production of vulcanized micro-porous sole rubbers and rubber technical articles. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ISO R 527 |
Stir SpA L 70 BZ (PVC) Application: Pipes and semi-rigid profilesInformation provided by STIR SpA |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Teknor Apex Synres® SR 4000 Polypropylene Notes: The Specialty Compounding Division offers a proprietary line of mineral filled polyolefins, including talc and calcium carbonate filled polypropylenes. Typical applications include injection .. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Plastics Group Polifil® C-30 30% Calcium Carbonate-Reinforced Polypropylene Polifil® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, heat aging, good colorability, resist.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Plastics Group Polifil® RMC-20 20% Calcium Carbonate-Reinforced Polypropylene, High Impact Polifil® RMC series compounds are high impact polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, they possess good stiffness, heat agin.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Plastics Group Polifil® RMC-20V 20% Calcium Carbonate-Reinforced Polypropylene, High Impact, UV Stabilized Polifil® RMC-V series compounds are high impact, UV stabilized polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, these compounds retar.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow UNIVAL™ DMDD-6200 NT 7 High Density Polyethylene Resin (HDPE) Moderate swell Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDD-6200 NT 7 is a multipurpose polymer designed for the high speed production of blow molded containers used to package hous.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Amco Amalloy® B9336 Polymer Alloy Amco Amalloy B9336 is a clear performance copolymer with exceptional clarity and toughness.Stiff, with good tensile and flexural strength.Information provided by Amco Plastic Materials. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Americas Styrenics STYRON® 478 High Impact Polystyrene Product CharacteristicsGood glossExcellent balance of flow and stiffnessFood Contact CompliantUL Classification 94HBUSP Class VITypical ApplicationsAppliancesMedicalHousewaresConsumer electronicsIn.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Americas Styrenics STYRON® 484 High Impact Polystyrene Product CharacteristicsToughnessHeat resistanceGood stiffnessFood Contact CompliantUL Classification 94HBTypical ApplicationsLidsAppliances/RefrigerationPackaging/disposablesHousewaresInformation pr.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | cured, grit-blasted steel; ASTM D2095 |
3M Scotch-Weld™ SF100 Super Fast Instant Adhesive 3M™ Scotch-Weld™ Super Fast Instant Adhesives rely less on surface moisture for cure speed than standard cyanoacrylates. They are designed to join together difficult-to-bond plastics and rubbers, .. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ISO 527-1/-2 |
DSM Arnitel® PB581-H Polyether Ester Elastomer (European Grade)
(discontinued **) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Amco Amalloy® B9941 Polymer Alloy Amco Amalloy B9941 is a clear performance copolymer with exceptional clarity and toughness.Good flexural and tensile strength.Information provided by Amco Plastic Materials. |
|||
Tensile Strength at Break | 25.5 MPa | 3700 psi | ASTM D638 |
Chase Plastics CP Pryme® PPC100NB-10M Polypropylene Copolymer Information provided by Chase Plastics. |