Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
Niche Polymer PA66GF33N Nylon 66, 33% Glass Fiber Filled Information provided by Niche Polymer |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
Performance Polymers IPS II PPL-C4150 PEKK (Polyetherketoneketone) Linear 30 % Glass Fiber Reinforced Molding Grade Amber pelletsInformation provided by Infinite Polymer System II. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 1200 A 33 HS White 247 A Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear (Asia Pacific) LNP* Thermocomp* OC006 is a compound based on PPS - Linear resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6 LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF008S PA 6 (Asia Pacific) LNP THERMOCOMP* PF008S is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP OC006 PPS - Linear LNP* THERMOCOMP* OC006 is a compound based on PPS-Linear resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP PF008 PA 6 (Asia Pacific) LNP THERMOCOMP* PF008 is a compound based on Nylon 6 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RX99732C PA 66 LNP* Thermocomp* PDX-R-99732 is a Nylon 6/6 with proprietary fillers. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RX99732C PA 66 LNP* Thermocomp* PDX-R-99732 is a Nylon 6/6 with proprietary fillers. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
A. Schulman SCHULAMID® 66 GF33HS 33% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |