Polymer Property : Tensile Strength at Break = 1900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	13.1 MPa	1900 psi	Flow; DIN 53504
PolyOne OnFlex™ U 5365A-E0134 FG Thermoplastic Elastomer (TPE) OnFlex™ U 5365A-E0134 FG is a performance TPU alloy designed for use in injection molding application where FDA compliance and Overmolding onto PC, ABS and PC/ABS substrates are required.Properties..
Tensile Strength at Break	13.1 MPa	1900 psi	510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible B7501 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	13.1 MPa	1900 psi	510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible C8500 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	13.1 MPa	1900 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R263AM Polyvinyl Chloride + NBR (PVC+NBR) Information provided by PolyOne
Tensile Strength at Break	13.1 MPa	1900 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Geon™ Vinyl Flexible R5257A White 759 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
ExxonMobil Escorene® LD 720.92 Specialty Film Resin (discontinued **) Escorene Ultra LD 720 resins are high vinyl acetate copolymer specialty film resins designed for applications requiring outstanding heat sealability, along with excellent strength properties and tou..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
LyondellBasell MicrotheneÂ® F FN50100 Low Density Polyethylene General DescriptionMicrothene F polyolefin powders are ultra-fine, spherically shaped particles with narrow size distribution suitable for use in a broad range of specialty applications. Microthene..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
LyondellBasell PlexarÂ® PX2250 Extrudable Tie-Layer Resin, Anhydride Modified HDPE PlexarÂ® tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, s..
Tensile Strength at Break	>= 13.1 MPa	>= 1900 psi	ASTM D412 Method A
Seals Eastern 7204 Ethylene-Propylene Rubber Y267-Type EPDM for geothermal steam service. Ultra-Low compression set.Information provided by Seals Eastern, Inc.
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
Teknor Apex APEXÂ® 154 Polyvinyl Chloride, Flexible Notes: 80Â°C Jacket; RoHS Compliant Uses: Military Cable Jacketing; Non-flexible JacketingForms: Pellets Wire Types: Molded Components Agency Ratings: MIL C-915-C Additional Information: Temperatu..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
Teknor Apex APEXÂ® 3601-65 Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Agency Ratings: NSF 61 Forms: Pellets Additional Information: Second Generation SeriesInformation Provided by Teknor Apex
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D412
Teknor Apex MonpreneÂ® MP-1688A Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
Teknor Apex APEXÂ® 90-R471U-70-NT Polyvinyl Chloride, Flexible Uses: Medical/Healthcare Applications Forms: PelletsInformation Provided by Teknor Apex
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D412
Teknor Apex MonpreneÂ® MP-2880E Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D412
Teknor Apex MonpreneÂ® MP-2990 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D412
Borealis PC0787 Polyethylene Insulation Compound, Crosslinkable PC0787 is a flame retardant crosslinking polyethylene compound for low voltage insulation. PC0787 contains flame retardant additives to reduce normal flame spread characteristics so as to achieve a..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D412
Borealis PC0798 Polyethylene Insulation Compound, Crosslinkable PC0798 is a flame retardant crosslinking polyethylene compound for low voltage insulation. PC0798 is a halogenated, colorable, chemically crosslinkable copolymer compound which contains flame retar..
Tensile Strength at Break	13.1 MPa	1900 psi	500mm/min; ASTM D638 Type IV Specimen
Westlake EC4041AA Low Density Polyethylene WESTLAKE low-density polyethylene EC4041 is recommended for use in the boardstock coating industry. The resin has low neck-in and good drawdown characteristics. Coatings produced from EC4041 have ex..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
ExxonMobil LLDPE LL 1004YB Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1004YB is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. The grade contains a higher l..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
ExxonMobil LLDPE LL 5002.09 Linear Low Density Polyethylene Resin Product Description: LL 5002.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. LL 5002.09 also exhibits good toughness and environmental str..
Tensile Strength at Break	13.1 MPa	1900 psi	ISO 37
Alliance Polymers Viprene™ P90A-22U-BLK Thermoplastic Vulcanizate Elastomer Viprene™ P90A-22U-BLK is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac..
Tensile Strength at Break	13.1 MPa	1900 psi	ISO 37
Alliance Polymers Viprene™ P90A-22U-NAT Thermoplastic Vulcanizate Elastomer Viprene™ P90A-22U-NAT is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac..
Tensile Strength at Break	13.1 MPa	1900 psi
3M Scotch-Weld™ DP8010 Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polypropyl..
Tensile Strength at Break	13.1 MPa	1900 psi
3M SMS Heat Shrink Tubing 3M Heat Shrink Tubing SMS is a co-extruded, dual wall product. It is a composite of a polyolefin shrinkable outer wall and a thermoplastic adhesive inner wall. SMS tubing does not degrade when expos..
Tensile Strength at Break	13.1 MPa	1900 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
3M Dyneon™ FC 2122 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FC 2122 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formul..
Tensile Strength at Break	13.1 MPa	1900 psi
Abatron AboCast/AboCure 8007-2 High-Grade Polysulfide-Epoxy Flexible Membrane Sealant and Joint-Filler AboCast/AboCure 8007-2 is a 2-part polysulfide-epoxy solventless system. It is weather- and water-proof, flexible, and acid, alkali, and fuel resistant. Uses: Filling joints and cracks in exposed s..
Tensile Strength at Break	13.1 MPa	1900 psi
3M EPS-400 Heat Shrink Tubing 3M Heat Shrink tubing EPS-400 is a medium-wall, semi-rigid tubing offering the advantages of integral, adhesive-lined construction. The tubing is made from flame-retardant, flexible polyolefin with ..
Tensile Strength at Break	13.1 MPa	1900 psi	ASTM D638
Teknor Apex APEX® 90-A471R-70-NT Polyvinyl Chloride, Flexible Features: DEHP Plasticizer; Radiation (Gamma) Resistant; Radiation Sterilizable Uses: Medical/Healthcare Applications; Tubing Processing Method: Extrusion Forms: PelletsInformation Provided by Tekno..