Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 11.0 MPa | 1600 psi | TM R050-36 |
Resinlab® EP1112NC Clear Electronic Grade Epoxy Encapsulant Resinlab™ EP1112NC Clear is a two part unfilled fast curing electronic grade epoxy encapsulant designed for small to medium sized castings. EP1112NC Clear is a modified version of the standard EP11.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D412 |
Multibase TPSiV™ 3040-65A Thermoplastic Silicone Vulcanizate These materials are a novel family of TPV products based on cross-linked silicone rubber dispersed into various engineering thermoplastics. The dispersion of the silicone internal phase is produced.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527 |
Polimeri Europa Riblene® GP 26 Low Density Polyethylene - Coating Grade Riblene GP 26 is a high fluidity low density polyethylene resin (LDPE).Main Applications: Riblene GP 26 is suitable for coating applications where low neck-in and high draw-down are key factors. F.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D 638 |
NOVA Chemicals Novapol® LF-0718-A-INJECTION LDPE Injection Molding Resin LF-0718-A complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food. LF-0718-A is subj.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible D75M0 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
SABIC HP7022 Low Density Polyethylene for Injection Molding Product Description: HP7022 is a Low Density Polyethylene offering a unique combination of consistent processability, flexibility and toughness. Articles manufactured from HP7022 exhibit excellent.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
LyondellBasell Petrothene® NA206000 Low Density Polyethylene ApplicationsPETROTHENE NA 206-000 is an extrusion coating resin especially recommended for high-speed, light weight coating applications. The resin can be drawn to a 3 lb/ream coating weight at lin.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527-1, -2 |
LyondellBasell Hifaxâ„¢ CA244 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CA244 high melt flow, 850 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has an excellent combination of stiffness, processability and dynamic.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 8620 PP SABIC® PPcompound 8620 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was origin.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D412 |
Sumitomo Chemical ESPOLEX® 4832 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
Borealis LE0315 Polyethylene Compound, Crosslinkable, Semiconductive LE0315 is an Easy Strippable Semi conductive Insulation Shield for EPR Insulated, Medium Voltage (5-46 kV) Cables. Strip forces range from 5 to 10 lbs/0.5". Specifications: LE0315 meets the applica.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 500mm/min; ASTM D638 Type IV Specimen |
Westlake EM1550AA Low Density Polyethylene WESTLAKE low-density polyethylene EM1550 is a low-density formulation used for injection molding applications.Application/UsesFlexible medicalLidsMedicalFDA: This material complies with FDA regulati.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
Teknor Apex Vidux® 100-1A Polyvinyl Chloride, Flexible Forms: PelletsInformation Provided by Teknor Apex |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds GS 6530 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds GS 7010 Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | Across Flow; ASTM D412 |
ExxonMobil Santoprene® 121-80 Thermoplastic Elastomer A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide ran.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds PH 55 Flexible PVC, Transparent Extrusion Transparent profiles |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds PH 60/A Flexible PVC, Transparent Extrusion Profiles, UL Class V2 |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO R 527 |
Fainplast Compounds PM 55 Flexible PVC, Lead Free Gaskets for frames |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
Aclo Accucomp Polyethylene HD0205L High Density |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | TM R050-36 |
Resinlab® EP1290 Gray Mineral Filled Epoxy Adhesive Resinlab™ EP1290 Gray is a two part mineral filled epoxy adhesive designed for bonding metals and plastics. It cures at room temperature to a tough, semi-flexible material. It has good wetting to m.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 25mm/min; ISO 527 |
Borealis LE7704 Polyethylene Compound, Semiconductive, Thermoplastic LE7704 is a thermoplastic black polyethylene compound, specially designed for semiconductive screen applications. Applications: LE7704 is intended for semiconductive applications in medium voltage.. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | 25mm/min; ISO 527 |
Borealis LE7710 Polyethylene Compound, Semiconductive, Thermoplastic LE7710 is a thermoplastic black polyethylene compound, specially designed for semiconductive screen applications. Applications: LE7710 is intended for semiconductive applications in medium voltage .. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | Fuel Resistance |
LG Chemical NBR 8300 High Acrylonitrile Polymer Description: NBR 8300 is a copolymer of butadiene-acrylonitrile and the powdered nitrile elastomer manufactured by advanced emulsion polymerization technology of Goodyear and LG Chem. NBR 8300 has .. |
|||
Tensile Strength at Break | 11.0 MPa | 1600 psi | |
Master Bond UV15X-6NONMED-2 Abrasion Resistant UV Curable Compound Description: Master Bond Polymer System UV15X-6NONMED-2 is a newly developed one component clear, non-yellowing, UV curable urethane elastomer system possessing high flexibility and abrasion resista.. |