LyondellBasell Hifaxâ„¢ CA244 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CA244 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ CA244 high melt flow, 850 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has an excellent combination of stiffness, processability and dynamic impact characteristics. It was designed primarily for use in painted automotive bumper fascia applications where material flow is an important consideration. Uses: Automotive exterior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ISO 1183 |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 230 °C |
16 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-1, -2 |
| Elongation at Break | 500 % | 500 % | ISO 527-1, -2 |
| Elongation at Yield | 14 % | 14 % | ISO 527-1, -2 |
| Flexural Modulus | 0.848 GPa | 123 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.90 kJ/m² @Temperature -40.0 °C |
1.86 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 33.0 kJ/m² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 25.0 J @Temperature -30.0 °C |
18.4 ft-lb @Temperature -22.0 °F |
Instrumented; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.80 % | 0.80 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.10 % @Temperature 121 °C, Time 3600 sec |
1.10 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Ovation Polymers Opnyl OP66GF33 Nylon 66, 33% Glass Reinforced, Dry
- Shell Carilon® DB6F5G40 Polyketone, Flame-Retarded (V-0), 20% Glass-Reinforced Injection Molding Grade (disco
- Quadrant EPP Duratron® PEI U1000 Extruded Unfilled Polyetherimide (ASTM Product Data Sheet)
- Lubriplate H0-1 Petroleum-Based Heavy-Duty Hydraulic Oil
- SABIC Innovative Plastics ULTEM 1010F PEI
- The NanoSteel® Company SHS 9172 TWAS Steel Alloy, Cored Wire
- American Elements A-MITE™ Aluminum Oxide Nanopowder
- Zotefoams Plastazote® LD50CN Conductive Low Density Polyethylene Foam
- ChevronTexaco Gear Compounds EP, ISO 680
- Overview of materials for Nylon 66/6, Mineral Reinforced
Copyright © lookpolymers.com All Rights Reserved