Polymer Property : Tensile Strength at Break = 96.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Oxford Polymers PEEK 450-INJ-Black PEEK Product Description: Polyetheretherketone, general purpose injection molding grade Processing and Delivery Form: Pellets and Injection MoldingAdditives: Carbon black Special Characteristics: Precol..
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Polymer Resources NY66-M40-[color]-H Nylon 66, 40% Mineral Filled, Heat Stabilized Nylon 66, 40% Mineral Filled, Lubricated, Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon ..
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Polymer Resources PPX-FRG20 Modified-PPO, V-1 Flame Retardant, 20% Glass Reinforced Modified-Polyphenylene Oxide, V-1 Flame Retardant, 20% Glass ReinforcedFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing condu..
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Polymer Resources TP-GFMF1 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced, Flame Retardant Polybutylene Terephthalate, 40% Glass/Mineral Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test..
Tensile Strength at Break	96.5 MPa	14000 psi	5.1 mm/min; ASTM D638
PolyOne Edgetek® PS-20GF/000 NATURAL Polybutylene Terephthalate (PBT) Information provided by PolyOne
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Ravago Manufacturing Americas Hylon® N1040ML Nylon 6/6 (DAM) (discontinued **) Information provided by Ravago.
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Chase Plastics CP Pryme® N310L (Dry) Nylon 6, 10% Glass Fiber Reinforced, Lubricated, Recycled Content Features: LubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Chase Plastics CP Pryme® PC320GR Polycarbonate (Utility Grade), 20% Glass Fiber Reinforced, Mold Release Information provided by Chase Plastics.
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman.
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
A. Schulman SCHULADUR® A GF15 15% Glass Fiber Reinforced PBT Information provided by A. Schulman.