Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 73.0 MPa | 10600 psi | |
Plastcom SLOVAMID 66 LI PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | |
Plastcom SLOVAMID 66 LI TS PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® 144 PC UL rated HB. 200 series recommended when V-2 rating required. 10.5 MFR. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer be supported with bioco.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD1014 PC Copolymer (Europe-Africa-Middle East) 7 MFR LEXAN HFD Copolymer |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD1034 PC Copolymer 7 MFR LEXAN HFD Copolymer UV-stabilized, available in transparent colors only |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD1034 PC Copolymer (Asia Pacific) 7 MFR LEXAN HFD Copolymer UV-stabilized, available in transparent colors only |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPS4 PC (Europe-Africa-Middle East) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI).EtO, steam, e-beam, and gamma sterilizable... |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® ML6430 PC Copolymer (Europe-Africa-Middle East) Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colorsThis data was supplied by SABIC-IP for the Europe-Afri.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SLX1431D PC Copolymer (Europe-Africa-Middle East) Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. Available in diffusion colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SLX2431D PC Copolymer (Asia Pacific) Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in diffusion colors.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SLX2431D PC Copolymer (Europe-Africa-Middle East) Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in diffusion colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle Ea.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® SLX2471T PC Copolymer Medium viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HFD1014 PC Copolymer 7 MFR LEXAN HFD Copolymer |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific) LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pac.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL V02570 PPE+HIPS Noryl* V02570 is a 25% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RAL22I PA 66 LNP* LUBRICOMP* RAL22I is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant, High Impact. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RL002 PA 66 LNP LUBRICOMP* RL002 is a compound based on Nylon 66 resin containing 10% PTFE. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RL003 PA 66 LNP* LUBRICOMP* RL003 is a compound based on Nylon 66 resin containing 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP UAL22S PPA LNP* LUBRICOMP* UAL22S is a compound based on Polyphthalamide resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON WSF42 PBT (Europe-Africa-Middle East) LNP*STAT-KON* WSF42 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Stainless Steel Fiber. Added features include: Electrically Conductive. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp MF006ASJ PP LNP THERMOCOMP* MF006ASJ is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized, Healthcare.This data was supplied by SABIC-IP f.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL N300X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0. High heat. Dielectric strength. Dimensional stability. Suitable for E/E applications. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL PKN4752 PPE+PS PPE+PS blend. High Heat. Translucent with yellow tint in natural color. FDA compliant. Extrusion and Injection Molding. Typical applications include High Performance Food Packaging, Electronics and .. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | ISO 527 |
Azoty Tarnow™ TARNOFORM 300 GF6 BK POM 30% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A... |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 5mm/min; ISO 527-2 |
Denka TX-100S Transparent Resin Polymer (MS resin) Methyl Methacrylate Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HP4NR PC Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no m.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HP4NR PC (Asia Pacific) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no m.. |
|||
Tensile Strength at Break | 73.0 MPa | 10600 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SD9705 PC Copolymer (Europe-Africa-Middle East) High visocisty PC Copolymer, low smoke, flame retardant resinThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |