Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 35.0 MPa | 5080 psi | |
Plastcom SLOVALEN PC 51 GF 10 PP, 10% glass fibre FeaturesModified copolymer PP for injection moulding, chemically reinforced with 10% glass fibre, with high strength, rigidity and toughness, adapted thermal properties, decreased shrinkage. Suitabl.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® G360 ABS (Europe-Africa-Middle East) CYCOLAC G360 is a high flow, high impact, medium to high heat resistant injection moulding ABS grade. It is recommended for large or complex parts in the automotive or electrical power tool segments.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® GPM5500S ABS (Europe-Africa-Middle East) CYCOLAC GPM5500S is a multi purpose injection moulding grade, equal to GPM5500 but equiped with anti static agents, providing a favourable balance of engineering properties. CYCOLAC GPM5500S has a w.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® GPM5500U ABS (Europe-Africa-Middle East) CYCOLAC GPM5500U is a UV stabilized multi purpose injection moulding grade, providing a favourable balance of engineering properties. CYCOLAC GPM5500U has a wide processing window. It is recommended.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG8000SR ABS (Europe-Africa-Middle East) This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG94 ABS (Europe-Africa-Middle East) Superior flow, injection molding ABS. Good impact. For thin-wall applications. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® MG94U ABS High flow, UV stabilized ABS molding grade |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP COLORCOMP A1000H ABS LNP* COLORCOMP* A1000H is an unfilled compound based on ABS. Added feature of this grade is: Healthcare. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | STN EN ISO 527-2 |
Plastcom SLOVALEN PH 91 T 20 Polypropylene Homopolymer, 20% Micronized Talc FeaturesModified homopolymer PP for injection moulding with the content of 20% micronized, floated, chemically modified talc. General application in all industry branches - packing material, garden.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO R 527 |
Fainplast Compounds RH 208 Rigid PVC, Antishock Extrusion Medium antishock profiles |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO R 527 |
Fainplast Compounds RK 325 Rigid PVC, Extrusion Lead Free Verticle curtains |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO R 527 |
Fainplast Compounds RKS 320 Rigid PVC, Antishock Extrusion Lead Free Various profiles, antishock |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | DIN 53504 |
Huntsman IROGRAN® A 70 H 4673 M Polyester-Based TPU-Injection Molding Grade Introduction: IROGRAN A 70 H 4673 M is a soft polyester based thermoplastic polyurethane intended for injection molding applications. IROGRAN A 70 H 4673 M is part of the HUNTSMAN injection molding .. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | |
LATI Latamid 12 H FE90 PA 12, Heat Stabilized Polyamide 12 (PA12) based compound. Heat stabilized. Magnetizable filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | |
LATI Latigray 37 B01-01 CX/35 Bio-Polymer Radiopaque compound based on Bio-Polymer (PLA, PHB, ...). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | |
LATI Latiohm 83-07 PD11 CNT PA12, Impact Modified Semiconductive/dissipative product based on Polyamide 12 (PA12), impact modified. Carbon nanotubes. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC Xenoy HX6600HP is PBT based semi-crystalline blend with balanced flow and impact properties. Improved chemical resistance against lab disinfectants and chemicals for healthcare enclosure and housing.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Xenoy® X2420 PC+POLYESTER (Asia Pacific) Xenoy*X2420 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and impact strength. X2420 has enhanced melt flowability, impact ductility and broad co.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON SX90398 PA 12 LNP STAT-KON* SX90398 is a compound based on Nylon 12 resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL PX1005X PPE+HIPS (Europe-Africa-Middle East) Noryl PX1005X is an unfilled, low heat resistance, halogen free (according VDE/DIN 472 part 813) flame retardant material. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® XE 4128 black 9221 PA610 Product description: Grilamid XE 4128 black 9221 is a modified high viscosity Polyamide 610 for extrusion as well as injection molding. A characteristic of tubes made out of this material is the hig.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-717C ABS Medium impact |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50mm/min; ISO 527-2 |
Denka TP-801 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® L 25 W 40 ESD PA12 Product Description: Grilamid L 25 W 40 ESD is a high viscosity, anti-static highly flexible extrusion grade of Polyamide 12 (PA12). Grilamid L 25 W 40 ESD is plasticized and heat stabilized The inh.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-747F ABS - Extrusion Refrigerator |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM-D638 |
Braskem AC59 HDPE Monofilament Polyethylene Homopolymer AC59 resin is a high-density polyethylene homopolymer produced by the solution process and designed for monofilament applications. It contains antioxidant additives. Its applications include: film .. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
Arkema Group Pebax® MV 3000 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MV 3000 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This hydrophilic grade when extruded into either a thin film or laminated on .. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437G20M10CL Glass/Mineral Reinforced Coupled |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
3M Dyneon™ PFA FLEX 8502 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules Dyneon™ PFA-FLEX UHP family exhibits improved environmental stress crack resistance to stress cracking agents such as fluorsurfactants and fluorosurfactant-containing chemicals. In addition, this f.. |
|||
Tensile Strength at Break | 35.0 MPa @Temperature 32.0 °C |
5080 psi @Temperature 89.6 °F |
|
Beijing Evergrow Resources UHMW PE Powder Ultra-high molecular weight polyethylene (UHMWPE) is an outstanding engineering plastic. It’s characterized by the following properties.Features:Very high abrasion resistanceVery high impact streng.. |