Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 172 MPa | 24900 psi | ASTM D638 |
Performance Polymers IPS II PPL-C4219 PEKK (Polyetherketoneketone) Linear Wear Grade Black pellets; Carbon fiber/PTFE/Graphite compoundInformation provided by Infinite Polymer System II. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Edgetek® NN-30GF/000 Polyamide 66 (Nylon 66) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | ASTM D638 |
PolyOne Stat-Tech™ NN-20CF/000 Black HS Polyamide 66 (Nylon 66) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||
Tensile Strength at Break | 172 - 207 MPa | 25000 - 30000 psi | Copper butt joint |
Lucas-Milhaupt BRAZE 450 Silver Based Cadmium Free Filler Metal Characteristics:Braze 450 is an intermediate temperature cadmium free silver brazing filler metal with sufficient melting range (145EF) to properly braze joints with the range of fits encountered in.. |
|||
Tensile Strength at Break | 172 - 207 MPa | 25000 - 30000 psi | Copper butt joint |
Lucas-Milhaupt BRAZE 650 (Easy) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel.. |
|||
Tensile Strength at Break | 172 - 207 MPa | 25000 - 30000 psi | Copper butt joint |
Lucas-Milhaupt BRAZE 750 (Hard) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel.. |
|||
Tensile Strength at Break | 172 MPa | 25000 psi | ASTM D638 |
Techmer ES Electrafil® J-1305/CF/20 PPS |
|||
Tensile Strength at Break | 172 MPa | 25000 psi | ASTM D638 |
Techmer ES Electrafil® J-1305/CF/30/TF/15 BK PPS |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific) High flow Ultem blends for thin wall application |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DE006 PC (Europe-Africa-Middle East) LNP* Stat-kon* DE006 is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 172 MPa | 25000 psi | ASTM D638 |
Techmer Lehvoss Compounds Luvotech™ J-4/30/V0 BK2989 PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | ISO 527-1/-2 |
Polyplastic Armamid® PA6 GF 30 HS-901 Nylon, 30% Glass Filled Injection molding, heat stabilizedInformation provided by PolyPlastic Group. |
|||
Tensile Strength at Break | 172 MPa | 24900 psi | ACMA Test #4 / DIN EN 843-1 |
CeramTec 614/698 Alumina, 96% 614/698 (96%) is a high-strength alumina with good mechanical properties, as well as good wear and chemical resistance. It also features excellent electrical properties. 614 is white; 698 is pink. |