SABIC Innovative Plastics LNP STAT-KON DE006 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DE006 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* DE006 is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 172 MPa | 24900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 19.6 GPa | 2840 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 229 MPa | 33200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
3.89 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
32.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Radici Radilon® CA RV300L (cond.) Nylon 66/6
- H.C. Starck Amperit® 744 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2)
- Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours
- Corning 8870 Potash Lead Crushed Glass
- EMS-Grivory Grivory® GVL-4H nat PA*-GF40
- Eurostar Staramide BK8 PA6, 40% Mineral Fiber Filled, Injection Molded
- DuPont Performance Polymers Hytrel® RS R4275 BK316 Polyester Elastomer TPC-ET
- Adamas Adalon® 118 PTFE, 23/2% Carbon/Graphite Filled
- Fainplast Compounds RI 548/H Rigid PVC, Antishock Injection Molding
Copyright © lookpolymers.com All Rights Reserved