Polymer Property : Tensile Strength at Break = 17.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	17.0 MPa	2470 psi	STN EN ISO 527-2
Plastcom PLASTALEN® EQ 18 N Polyethylene Impact modified PE for extrusion. Delivered in black color.Information Provided by Plastcom spol. s r.o.
Tensile Strength at Break	<= 17.0 MPa	<= 2470 psi	ISO/R527
Polykemi AB POLYfill PPC B10075 Polypropylene Copolymer, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527-1, -2
LyondellBasell Hostacomâ„¢ BR712GC Polypropylene Copolymer Description: Hostacomâ„¢ BR712GC conventional melt flow, 1,300 MPa flexural modulus, UV-stabilized, mineral-filled polypropylene copolymer has an excellent balance of stiffness, impact and weathe..
Tensile Strength at Break	17.0 MPa	2470 psi	after 7days @113Â°C; UL 1581
SABIC Innovative Plastics NORYL WCD801A PPE-TPE Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements..
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Tensile Strength at Break	>= 17.0 MPa	>= 2470 psi	250mm/min; ISO 527
Borealis LE4201R Polyethylene Insulation Compound, Crosslinkable LE4201R is a crosslinkable natural polyethylene compound, specially designed for insulation applications. Applications LE4201R is intended for insulation of XLPE power cables with rated voltages up..
Tensile Strength at Break	>= 17.0 MPa	>= 2470 psi	250mm/min; ISO 527
Borealis LE4244R Polyethylene Insulation Compound, Crosslinkable LE4244R is a crosslinkable natural polyethylene compound, specially designed for insulation applications. This product is only available in certain periods. Applications: LE4244R is intended for in..
Tensile Strength at Break	>= 17.0 MPa	>= 2470 psi	250mm/min; ISO 527
Borealis Supercure™ LC8205R Polyethylene Insulation Compound, Crosslinkable Supercure™ LC8205R is a crosslinkable natural polyethylene compound, specially designed for insulation applications. Applications: Supercure™ LC8205R is intended for insulation of XLPE power cabl..
Tensile Strength at Break	>= 17.0 MPa	>= 2470 psi	ISO R 527
Fainplast Compounds GS 7325 Flexible PVC, Electrical Plugs Plugs
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PMP 81 Flexible PVC, Extrusion Modified with PU Under sheathing PVC/PU
Tensile Strength at Break	17.0 MPa	2470 psi	ISO 527-1/-2
DuPont Performance Polymers Hytrel® G4774 Polyester Elastomer TPC-ET (Unverified Data**) 47 Shore D Standard Performance Polyester Elastomer with Heat Ageing ProtectionHytrel G4774 is a medium modulus grade with nominal hardness of 47D. It contains discoloring stabilizer. It can be proc..
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds MPH 78 Medical Flexible PVC, Extrusion Tubolar apparatus
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds MPH 78/H Medical Flexible PVC, Extrusion Technical tubes no DOP
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PH 70/AS Flexible PVC, Transparent Extrusion Food belt carriers
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PH 75 Flexible PVC, Transparent Extrusion Transparent profiles and pipes
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds PK 91 Flexible PVC, Lead Free Fencing
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Arkema Group LOTRYL® 24 MA 005 Copolymer Ethylene - Methyl Acrylate LOTRYL® 24 MA 005 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the high methyl acrylate content, LOTRYL® 24 MA 005 is a poly..
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436W40L Wollastonite Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0334C10L1 Calcium Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0336C10L Calcium Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0336C10L1 Calcium Reinforced
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436T40L Talc Reinforced
Tensile Strength at Break	>= 17.0 MPa	>= 2470 psi	ASTM D638
UBE UBESTA® 3035JX47 Plasticized Industrial Grade Nylon 12 Description: UBE UBESTA® Industrial grade Nylon 12Comments: conductiveInformation provided by UBE.
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D638
Petroquimica Triunfo Trithene® SX 9003 MDPE - Blow Molding The Trithene® SX 9003 resin is a medium density polyethylene (MDPE) with high molecular weight that presents excellent mechanical properties, thermal stability and high stiffness when compared with..
Tensile Strength at Break	17.0 MPa	2470 psi	ASTM D-412
Dynasol Solprene® 416 Thermoplastic Rubber SBS Dry Solprene 416 is a radial styrene/butadiene block copolymer having 30% of styrene content, most of it forming a polystyrenes block which gives the polymer a thermoplastic behavior. It develops proper..
Tensile Strength at Break	17.0 MPa	2470 psi	Across Flow; ASTM D412
ExxonMobil Geolast® 703-45 Thermoplastic Elastomer A hard, black, oil resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good hot air and hot oil resistance for use in a wide range of applic..
Tensile Strength at Break	17.0 MPa	2470 psi	ISO R 527
Fainplast Compounds MPH 75/D Medical Flexible PVC, Extrusion Technical tubes no DOP