Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 151 MPa | 21900 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 LNP* LUBRICOMP* RFL36L is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Low Extractible. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFL36L PA 66 (Asia Pacific) LNP* Lubricomp* RFL36L is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AR9200 PEI 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AR9200 PEI (Asia Pacific) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RF007ES PA 66 LNP* THERMOCOMP* RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66 LNP* THERMOCOMP* RFB66 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 30% Glass Bead. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66 (Asia Pacific) LNP* Thermocomp* RFB66 is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WC006 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WC006 is a compound based on Polybutylene Terephalate resin containing Carbon Fiber. |
|||
Tensile Strength at Break | 151 MPa | 21900 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp LF004 PEEK LNP THERMOCOMP* LF004 is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |