Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 14.7 MPa | 2130 psi | ISO 37 |
PolyOne OnFlex™ U 5355A-S0014 Thermoplastic Elastomer (TPE) OnFlex™-U thermoplastic elastomer compounds are based on thermoplastic polyurethane elastomers (TPE-U). The OnFlex™-U 5300 series are based upon alloys of SEBS and TPU, combining the advantages of.. |
|||
Tensile Strength at Break | 14.7 MPa @Thickness 2.00 mm |
2130 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
LG Chemical KEYFLEX BT 3028D Ester Type TPE Description: Injection Molding, TPC-ET, Functional, Fast Molding, Low ModulusApplication: Automotive Interior, Soft Touch GripsCAS: 37282-12-5Information provided by LG Chemical |
|||
Tensile Strength at Break | >= 14.7 MPa | >= 2130 psi | |
Sibur O-40 Compound 239 Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p.. |
|||
Tensile Strength at Break | 14.7 MPa | 2130 psi | ASTM D638 |
Teknor Apex APEX® 89-P180-B Polyvinyl Chloride, Flexible Notes: 80°C Jacket; RoHS CompliantFeatures: Flame Retardant; Low gloss; Low Temperature Flexibility Uses: Cable JacketingAgency Ratings: UL 62 Forms: Pellets Wire Types: SJT; ST; SVTInformation P.. |
|||
Tensile Strength at Break | 14.7 MPa | 2130 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SC 6501 Toughened Polystyrene Characteristics Excellent melt strength Extremely tough Easy printability Easy miscibility with most grades of polystyrene Processing Extrusion Thermoforming Injection MoldingApplications Impac.. |
|||
Tensile Strength at Break | 14.7 MPa | 2130 psi | ISO 37 |
Alliance Polymers Viprene™ G45D-32U-BLK Thermoplastic Vulcanizate Elastomer Viprene™ G45D-32U-BLK is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 14.7 MPa | 2130 psi | ISO 37 |
Alliance Polymers Viprene™ G45D-32U-NAT Thermoplastic Vulcanizate Elastomer Viprene™ G45D-32U-NAT is a UV and Heat Stabilized TVP (Thermoplastic Vulcanizate Elastomer). This material can be easily processed by extrusion or injection molding. It exhibits easy flowing charac.. |
|||
Tensile Strength at Break | 14.7 MPa | 2130 psi | ASTM D638 |
Asahi Glass AFLAS® 150E TFE/P Fluoroelastomer AFLAS® 100/150 fluoroelastomers are alternating copolymers of tetrafluoroethylene and propylene. They offer 1) excellent heat resistance, 2) exceptional chemical resistance especially to bases and .. |