Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics EXTEM UH1006M TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical Resistant |
|||
Tensile Strength at Break | <= 105 MPa | <= 15200 psi | ISO/R527 |
Polykemi AB POLYsan FL100 F35 SAN, Glass Fiber-Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | <= 105 MPa | <= 15200 psi | ISO/R527 |
Polykemi AB POLYshine PBT D223 GF10 FR PBT, Glass-Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Faradex ES003DE PEI LNP* Faradex* ES003DE is a Polyetherimide resin containing stainless steel fibers. Characteristics of this grade are EMI/RFI Shielding.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | <= 105 MPa | <= 15200 psi | ISO/R527 |
Polykemi AB POLYshine PBT D201 FB52 PBT, Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527 |
Nilit FRIANYL B63 L-HS-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced Nylon 6 for injection molding, improved fluidity, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-1/-2 |
Lanxess Pocan® B 3217 XF 000000 PBT, 16% Glass Fiber PBT, 16% glass fibers, injection molding, improved flowability, impact modified |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-1/-2 |
Lanxess Durethan® BKV 315 Z H2.0 901510 Nylon 6, 15% Glass Fiber PA 6 extrusion- and blow molding-grade with 15% glass fibers, branched/structural viscosity, elastomer-modified, good heat-ageing resistance, dry-impact modifiedApplication Examples: air intake hose.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL SE1GFN3 PPE+HIPS (Europe-Africa-Middle East) Noryl* SE1GFN3 is a 30% glass reinforced, injection moldable modified polyphenylene ether resin. Designed for improved dimensional stability and good flow , this resin also uses non-chlorinated, non.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP PFI12R PA 6 LNP* LUBRICOMP* PFI12R is a compound based on Nylon 6 resin containing 10% Glass Fiber, 2% Silicone. Added features of this material include: Wear Resistant, Mold Release. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics Ultem 1010K PEI (Europe-Africa-Middle East) Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ASTM D638 |
SABIC Innovative Plastics LNP LUBRILOY DF204 PC LNP* LUBRILOY* DF204 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added feature of th is grade is: Wear Resistant. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DEP42E PC LNP STAT-KON* DEP42E is a compound based on Polycarbonate resin containing 10% Carbon Fiber, 20% PTFE/Silicone. Added features of this material include: Easy Molding. Electrically Conductive, Wear.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DX05474 PC (Asia Pacific) LNP* Stat-kon* DX05474 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding, Flame Ret.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 830F PBT+PET (Europe-Africa-Middle East) PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® ENH4550 PBT 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® IQ507 PBT+PC (Europe-Africa-Middle East) Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® 6380U PBT+PET (Asia Pacific) XENOY 6380U is a 30% glass reinforced, UV stabilized grade, that combines high stiffness with improved ductility. The combination of mechanical properties at high and low temperatures and chemical r.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527 |
SABIC Innovative Plastics LNP VERTON MV006S PP (Asia Pacific) LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL NH7114 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH7114 resin is a 20% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve UL94 flame ratings while offering an exceptional balance of streng.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics ULTEM AUT200 PEI Transparent high flow Polyetherimide (Tg 217C). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperat.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-93 |
Wellman EcoLon® 2000-BK1 37% Post Consumer Compound Nylon 66 Description: Post Consumer Compound Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-93 |
Wellman Wellamid® GF13-66 22LH-NBK1 13% Glass Fiber Reinforced, General Purpose Nylon 66 Description: Glass Fiber Reinforced, General Purpose Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® LV-30H FWA black 9225 PA12-GF30 Product description: Grilamid LV-30H FWA black 9225 is a 30 % glass fiber reinforced, heat stabilized polyamide12 injection molding grade with the following special features: Stiffness combined with.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | ASTM D638 |
BLUESTAR 201G20 PBT, 20% Glass Filled Typical Applications: Energy saving lightingInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | v = 5 mm/min; ISO 527-2 |
CENTROPLAST CENTROMID 12 GF 30 Polyamide 12 30% glass fiber CENTROMID 12 GF 30 is a dimensionally stable and high strength material with good electrical insulating properties. Its applications include levers and valve parts.Information provided by CENTROPLA.. |
|||
Tensile Strength at Break | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® V9235 PET (Europe-Africa-Middle East) Valox heat stabilized, 15% Glass filled grade with mold release based on recycle PET. This grade is typically applied for business Machines applicationsThis data was supplied by SABIC-IP for the Eu.. |