- Polymer Property : Tensile Strength at Break = 10.0 MPa
Polymer Property : Tensile Strength at Break = 10.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
| Polimeri Europa Eraclene® MS 80 U High Density Polyethylene - Injection Molding Eraclene MS 80 U is a gas phase high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application. This grade has a narrow molecular weight distribution and a hig.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
| Polimeri Europa Flexirene® MS 20 A Linear Low Density Polyethylene Flexirene MS 20 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 20 A are characterized by optimum low tempe.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
| Polimeri Europa Flexirene® MS 26 A Linear Low Density Polyethylene Flexirene MS 26 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Parts made with Flexirene MS 26 A are characterized by optimum low tempe.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
| Polimeri Europa Flexirene® MT 40 A Linear Low Density Polyethylene Flexirene MT 40 A is a linear low density polyethylene (LLDPE), with antioxidants, suitable for injection molding application.Flexirene MT 40 A is characterized by a good processability and impact r.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Rate of 50 mm/min; ASTM D 638 |
| NOVA Chemicals Surpass® IFs932-R Octene SLLDPE Injection Molding Resin IFs932-R complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chem.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
| Polimeri Europa Eraclene® MS 80 High Density Polyethylene - Injection Molding Eraclene MS 80 is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.Eraclene MS 80 shows a good balance between processability and mechanical pro.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Injection molded parts; DIN 53504 |
| Huntsman IROGRAN® CA116-203 TPU-Polyester Introduction: IROGRAN CA116-203 is a high performance polyester based thermoplastic polyurethane intended for flat die extrusion applications. IROGRAN CA116-203 is part of the HUNTSMAN film and shee.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL WCP821 PPE-TPE Flexible Noryl* injection molding grade. Low specific gravity with very good non-halogenated flame retardant performance. Developed for evaluation in over-molding applications such as plugs, strain .. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Solvay Specialty Polymers Polidiemme® G/440 Thermoset Elastomer (TSE) Elastomer based compound crosslinkable by ambient moisture, consisting of a silane pregrafted base compound to be used with a catalyst masterbatch (Sioplas® method)Standards complying: Cenelec HD.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D412 |
| Teknor Apex Monprene® MP-2156E Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL WCD835 PPE-TPE (Europe-Africa-Middle East) Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| ELASTO UK Dryflex® 422401S SBS Based Material, 40D Hardness, Black The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | ISO R 527 |
| Fainplast Compounds CL 63/K Flexible PVC, Sheathing General purpose, opaque surface |
|||
| Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | ISO R 527 |
| Fainplast Compounds GA 63 Flexible PVC, Flame Retardant Sheathing Good flexibility |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds GS 56 Flexible PVC, Injection Molding for Footwear Vamp boots |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds GSO 70/33 Flexible PVC, Injection Molding for Footwear Soles, opaque surface |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds MPH 50/T Medical Flexible PVC, Extrusion Technical tubes and peristaltic pump segments no DOP |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness) AZDEL SuperLite® SL550700-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM-D638 |
| Braskem IC32 LLDPE Injection Molding Polyethylene Copolymer IC32 is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding. It offers good fluidity, excellent flexibility and tenac.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 |
| Arkema Group LOTADER® 6200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride LOTADER 6200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties (reactivity, fluidity), LOTADER 62.. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Addiplast Addilene H 420 K24 Polypropylene Homopolymer High densityInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D412 |
| 3M Scotchkote™ 80XRG 539 Urethane Elastomer Scotchkote Urethane Elastomer 80XRG 539 has been specifically developed as a fast curing elastomeric repair system with a high degree of flexibility for rebuilding and resurfacing rubber components... |
|||
| Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | |
| Beijing Evergrow Resources PTFE, 20% Glass Fiber Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with fillers of many different kinds. Amongst the m.. |
|||
| Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | |
| Beijing Evergrow Resources PTFE, 20% Glass Fiber, 5% Graphite Filled Filled PTFE article is manufactured by molding method with filled PTFE resin. Filled PTFE resin is manufactured by compounding PTFE granular resin with fillers of many different kinds. Broadly speak.. |
|||
| Tensile Strength at Break | >= 10.0 MPa | >= 1450 psi | ISO R 527 |
| Fainplast Compounds CL 76/E Flexible PVC, Sheathing General purposes |
|||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO R 527 |
| Fainplast Compounds PM 65/R Flexible PVC, Lead Free Extrusion modified with rubber |
|||