Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® VE-0812 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® SV-0167 ABS, Unreinforced Extrusion Grade Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D638 |
Samsung Cheil Industries Starex® VE-0812 ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Flexural Strength | 55.9 MPa | 8110 psi | s.d. 6.1 MPa, specimen 2.49 cm wide (s.d. 0.02 cm), 0.21 cm thick (s.d.01 cm), 3.8 cm span (s.d. 0 cm). Test conditions: Humidity 50%, Temp. 23°C. |
Schmelzer Industries Pearlveil 110-15 Fiberglass Veil Economical alternative for flat or shallow applications. Suitable for hand lay-up, pre-form molding, press molding, vacuum molding, and injection molding. Data provided by the manufacturer, Schmel.. |