Polymer Property : Flexural Strength = 33400 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	230 MPa	33400 psi	ASTM D790
NYCOA 5133 HS 33% Glass-Fiber Reinforced, Impact Modified, Heat Stabilized Nylon 66 Resin NYCOA 5133 HS is a 33% glass fiber reinforced, heat stabilized, impact modified, Nylon 66 suitable for injection molding. It offers excellent balance of mechanical, thermal and chemical properties; ..
Flexural Strength	230 MPa	33400 psi
Plastcom SLOVAMID 6 GF 33 PA6, 33% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 33% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-good..
Flexural Strength	230 MPa	33400 psi	STN EN ISO 178
Plastcom SLOVAMID 6 GF 35 Polyamide 6, 35% Glass Fiber FeaturesPA 6 for injection moulding, chemically strengthened with 35% of glass fiber, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-good..
Flexural Strength	230 MPa	33400 psi	ISO 178
PolyOne OnForce™ LFT LF9200-5001 RS Natural Polyphenylene Sulfide (PPS) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Flexural Strength	230 MPa	33400 psi	ISO 178
PolyOne OnForce™ LFT SF-40LCF/000 Black Polyphenylene Sulfide (PPS) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Flexural Strength	230 MPa	33400 psi	ISO 178
PolyOne OnForce™ LFT SF-40LGF/001 Natural Polyphenylene Sulfide (PPS) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. ..
Flexural Strength	<= 230 MPa	<= 33400 psi	ISO 178
Polykemi AB SCANAMID 66 A12^ F30 TF15 Nylon 66, Glass Fiber Reinforced, Modified Information provided by Polykemi AB
Flexural Strength	<= 230 MPa	<= 33400 psi	ISO 178
Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB
Flexural Strength	230 MPa	33400 psi	ASTM D790
PolyOne Nymax™ ND 1233 GF Black Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil..
Flexural Strength	230 MPa	33400 psi	ISO 178
Nilit FRIANYL A63 H-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength	230 MPa	33400 psi	2 [mm/min]; ISO 178
Akro-Plastic Akromid® S3 GF 30 4 (3552) PA 6.10 Dry, 30% Glass Filled (discontinued **) A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Flexural Strength	230 MPa	33400 psi
Lehmann & Voss LUVOCOMÂ® 1105-8167 PEEK, with carbon fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Dynamic stressed parts at high m..
Flexural Strength	230 MPa	33400 psi
Lehmann & Voss LUVOCOMÂ® 1501/CF/30-1 Polysulfone, with carbon fiber Applications: Automotive industry, office machinery, medical- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Chemical and hydrolysis resistance parts, non..
Flexural Strength	230 MPa @Strain 3.00 %	33400 psi @Strain 3.00 %	2 mm/min; ISO 178-A
Lanxess PocanÂ® T 7331 POS151 700226 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV stabilizedInformation provided by LANXESS.
Flexural Strength	230 MPa	33400 psi	ISO 178
Solvay TECHNYLÂ® A 218HP V50 PA66, 35% glass fiber, Conditioned Description: TECHNYLÂ® A 218HP V50 is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Benefits: The product off..
Flexural Strength	230 MPa	33400 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66 LNP LUBRICOMP* RX06480 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% Lubricants. Added feature of this material is: Wear Resistant.
Flexural Strength	230 MPa	33400 psi	ASTM D790
A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6 Information provided by A. Schulman.
Flexural Strength	230 MPa	33400 psi	ASTM D790
Polyram PlusTek PA301G5 Nylon 6.6, Heat Stabilized, 25% Glass Fiber Heat stabilized, 25% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Strength	230 MPa	33400 psi	ASTM-D790
Polyram Polytron P60B01 Homopolymer Polypropylene, Chemically Coupled 60% LGF A chemically coupled 60% LGF reinforced black PP, heat stabilized for high temperature applications such as under the hood automotive parts.Information provided by Polyram Ram On Ind.
Flexural Strength	230 MPa	33400 psi	ASTM-D790
Polyram Polytron P60B04 Homopolymer Polypropylene, Chemically Coupled 60% Long Glass Fiber A CHEMICALLY COUPLED PP 60% LONG GLASS FIBER WITH EXTRA LOAD OF ADDITIVES FOR DILUTION.Information provided by Polyram Ram On Ind.
Flexural Strength	230 MPa	33400 psi	ISO 178
Polyram Polytron P60B04-S Polypropylene, 60% Long Glass Fiber A chemically coupled polypropylene 60% long glass fiber with extra load of additives for dilution.Information provided by Polyram.
Flexural Strength	230 MPa	33400 psi	ASTM-D790
Polyram Polytron P60B11 Homopolymer Polypropylene, Chemically Coupled 60% LGF A chemically coupled 60% LGF reinforced black PP, heat stabilized for injection molding applications.Information provided by Polyram Ram On Ind.
Flexural Strength	230 MPa	33400 psi	ISO 178-93
Wellman Wellamid® GF33-66 XE-BKDX9 33% Glass Fiber Reinforced Nylon 66 Description: Glass Fiber Reinforced Nylon 66Information provided by Wellman.
Flexural Strength	230 MPa	33400 psi	cond; ISO 178
DSM Novamid® 1013G45 1 NA PA6-GF45 45% Glass Reinforced, Injection Molding
Flexural Strength	230 MPa	33400 psi	cond; ISO 178
DSM Novamid® 1013GH45 1 NA/BK701 PA6-GF45 45% Glass Reinforced, Heat Stabilized, Injection Molding
Flexural Strength	230 MPa	33400 psi	DAM; ISO 178
DuPont Performance Polymers Zytel® HTN FR52G30NH NC010 Polyphthalamide (PPA) (Unverified Data**) 30% Glass Reinforced Flame Retardant Non-Halogenated PPA High Performance Polyamide Zytel HTNFR52G30NH NC010 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin. It..
Flexural Strength	230 MPa	33400 psi	2 mm/min; ISO 178
Eurostar Staramide BG6U PA6, 30% Glass Fiber Filled, UV Stabilized, Injection Molded Staramide BG6U is an UV Stabilized, 30% Glass Fiber Reinforced, Polyamide 6, Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	230 MPa	33400 psi	2 mm/min; ISO 178
Eurostar Staramide BG6 PA6, 30% Glass Filled, Injection Molded BG6 is a 30% Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Flexural Strength	<= 230 MPa	<= 33400 psi	cond., 3.5% flexure; ISO 178
Azoty Tarnow™ Tarnamid® T-27 GF50 Polyamide 6 - Glass Fiber Reinforced 50% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High..