Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 14.0 MPa | 2030 psi | ASTM D790 |
Multibase Multi-Flex® TPE D 4310 Multi-Flex® D 4310 Natural was designed to replace Himont's CA 53 G material. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | ASTM D790 |
NYCOA 2366 Plasticized Copolyamide TPE NYCOA 2366 is an extremely flexible and transparent Nylon copolymer specifically developed for extrusion applications such as high-end fishing line, and flexible tubing. NYCOA 2366 possesses an extr.. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | STN EN ISO 178 |
Plastcom PLASTALEN® TPU N 85 LTS TPU Modified TPU. Use in all industry sectors. Delivered in the black.Information Provided by Plastcom spol. s r.o. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | |
Plastcom SLOVALEN PQ 91T 5 PP, 5% mineral filling FeaturesModified PP for injection moulding with the content of 5 % mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | |
Quadrant EPP Fluorosint® 207 PTFE + mica, compression moulded (ISO Data) This material has a food contact compliant composition which, in combination with the good mechanical performance, dimensional stability, sliding and wear properties and inherent outstanding chemica.. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | |
Quadrant EPP Semitron® ESd 500HR PTFE, static dissipative, extruded (ISO Data) Reinforced with a proprietary synthetic mica, Semitron ESd 500HR offers an excellent combination of low frictional properties, good dimensional stability and electrostatic dissipation. Whenever virg.. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | 3.5% Flexural Stress; DIN 53452 |
Fluorseals PTFE Unfilled Information provided by TEKU GmbH Fluorkunststoffe, a distributor of Fluorseals materials. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | Olsen; ASTM D747 |
UBE F320 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | Olsen; ASTM D747 |
UBE L719 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | Olsen; ASTM D747 |
UBE F019 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Flexural Strength | 14.0 MPa | 2030 psi | SAE J949 |
Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (2.5 mm Molded Thickness) AZDEL SuperLite® SL550900-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Strength | 14.0 MPa @Temperature 120 °C |
2030 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8253 HS PA6 (Dry) Ultramid 8253 HS is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased.. |
|||
Flexural Strength | 14.0 MPa @Temperature 120 °C |
2030 psi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8253 PA6 (Dry) Ultramid 8253 is an unfilled, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/o.. |
|||
Flexural Strength | 14.0 - 24.0 MPa @Strain 5.00 % |
2030 - 3480 psi @Strain 5.00 % |
ASTM D790 |
Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Flexural Strength | 14.0 - 24.0 MPa @Strain 5.00 % |
2030 - 3480 psi @Strain 5.00 % |
ASTM D790 |
Arkema Group KYNAR FLEX® 2750-01 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |