Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 9.00 MPa | 1310 psi | ASTM D790 |
SABIC MG200024 Linear Low Density Polyethylene for Compounding Product Description: MG200024 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution primarily suitable for compounding. It is in the powder form designed to give g.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | |
Pyrotek Pyrocast AR Castable Refractory Pyrocast AR is a fused silica castable refractory inert to liquid aluminum and its alloys. It is a high strength material offering resistance to erosion and mechanical damage. Parts cast from Pyro.. |
|||
Flexural Strength | 9.00 MPa @Temperature 100 °C |
1310 psi @Temperature 212 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AT-5001 Polyphthalamide (PPA) Resin, Dry as Molded
(discontinued **) AMODEL AT-5001 polyphthalamide resin is a neat ductile material that offers superior retention of properties after humid thermal aging, high impact at low temperature, and better mechanical properti.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | X-Direction; IPC-TM-650, 2.4.4 |
Rogers Corporation RO3730 Antenna Grade Laminate RO3730™ Laminates have the excellent thermo-mechanical properties and electrical characteristics that antenna designers need. The laminates have a dielectric constant of 3.0 and a loss tangent of.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | ASTM D790 |
SABIC M200024 Linear Low Density Polyethylene for Injection Molding Product Description: M200024 is a Linear Low Density Polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to give good f.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | at 3.5% strain; ISO 178 |
FKuR Kunststoff Bio-Flex® F 1130 Compostable PLA Blend The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any sta.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP YI001 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YI001 is a compound based on Polyester Elastomer containing Silicone. Added features include; Internally Lubricated. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | MD; ASTM D790 |
DuPont™ Nomex® Type 994, 125 mil Nominal Thickness Rigid Aromatic Nylon Board Type 994 is a densified, rigid board which has a unique combination of superior resistance to compression, even at elevated temperatures, along with relatively high oil absorption characteristics. T.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | MD; ASTM D790 |
DuPont™ Nomex® Type 994, 250 mil Nominal Thickness Rigid Aromatic Nylon Board Type 994 is a densified, rigid board which has a unique combination of superior resistance to compression, even at elevated temperatures, along with relatively high oil absorption characteristics. T.. |
|||
Flexural Strength | 9.03 MPa | 1310 psi | ASTM D790 |
Aclo Accucomp Polyethylene LD0102L Low Density |
|||
Flexural Strength | 9.03 MPa | 1310 psi | ASTM D790 |
Aclo Accucomp Polyethylene LD0109L Low Density |
|||
Flexural Strength | 9.00 MPa | 1310 psi | SAE J949 |
Azdel SuperLite® SL552000-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL552000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Strength | 9.00 MPa @Temperature 93.0 °C |
1310 psi @Temperature 199 °F |
ASTM Test |
BASF Ultramid® 8255 HS PA6 (Dry) Ultramid 8255 HS is a heat stabilized, impact modified type 6 nylon graft copolymer developed for both injection molding and extrusion applications. It exhibits varying levels of toughness and
fle.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | SAE J949 |
Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (3 mm Molded Thickness) AZDEL SuperLite® SL550800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Strength | 9.00 MPa | 1310 psi | SAE J949 |
Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (5 mm Molded Thickness) AZDEL SuperLite® SL551600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |