Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 140 - 160 MPa | 20300 - 23200 psi | Injection; ISO 178 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Flexural Strength | 140 - 160 MPa | 20300 - 23200 psi | Injection; ISO 178 |
Raschig Group 2572 AMC Glass fiber reinforced Polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, good abrasion stability, high flame retardance in combin.. |
|||
Flexural Strength | 120 - 160 MPa | 17400 - 23200 psi | Injection; ISO 178 |
Raschig Group 5562 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Flexural Strength | 120 - 160 MPa | 17400 - 23200 psi | Injection; ISO 178 |
Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Flexural Strength | 140 - 160 MPa | 20300 - 23200 psi | Injection; ISO 178 |
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe.. |
|||
Flexural Strength | 140 - 160 MPa | 20300 - 23200 psi | Injection and Compression; ISO 178 |
Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very .. |
|||
Flexural Strength | 140 - 160 MPa | 20300 - 23200 psi | Injection; ISO 178 |
Raschig Group SURAPLAST UPA 63 UP Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for.. |
|||
Flexural Strength | 140 - 160 MPa | 20300 - 23200 psi | At Rupture; ISO 178 |
Vyncolit 2950 W Novolac Phenolic Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group |