Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 180 MPa | 26100 psi | STN EN ISO 178 |
Plastcom PLASTAMID® 6 GF 25 002 PA6 reinforced with glass fiber PA 6 for injection molding, reinforced with 25% glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, .. |
|||
Flexural Strength | 180 MPa | 26100 psi | STN EN ISO 178 |
Plastcom SLOVASTER® B GF 30 FRL 4 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant FeaturesPBT with the content of 30% chemically coupled glass fiber and flame retardant based on bromine hydrocarbons. Anisotropy of shrinkage enables injection moulding of round, cylindrical or oth.. |
|||
Flexural Strength | <= 180 MPa | <= 26100 psi | ISO 178 |
Polykemi AB SCANMID 6 B22^ E F15 Nylon 6, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
Gromax PBT 4130-104D 30% Glass Fiber Filled Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent .. |
|||
Flexural Strength | 180 MPa | 26100 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics ULTEM CRS5201R PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. Resin is RoHS com.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
SABIC Innovative Plastics Valox® 420SE0 PBT (Europe-Africa-Middle East) 30% glass reinforced, UL94 V-0/5V rated. Numerous applications: edge trimmers, food mixer motor stator and commutator, cooling fan, connectors, bobbins, switches etc |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
Techmer ES HiFill® PA4/6 0206 Availability: North AmericaForms: PelletsFeatures: High Specific Gravity and Thermally ConductiveInformation provided by TP Composites, Inc. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Solvay TECHNYL® A 218W V30 Black FA PA66, 30% glass fiber, Conditioned Description: Polyamide 66, reinforced with 30% of glass fiber, for injection molding, heat stabilized, with improved hydrolysis resistance.Available in: EuropeProduct Applications: TECHNYL A 218W V3.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D638 |
A. Schulman PP 984 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 984 is a medium impact polypropylene used primarily for automotive parts subjected to impact.Information provided by A. Schulman. |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D638 |
A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Strength | 180 MPa | 26100 psi | Flexural Strain: 3.1%; ISO 178 |
Polyplastics Freqtis® C0511A (PPS/LCP), Molding Compound Both base resins (PPS and LCP) exhibit excellent heat resistance, dimensional stability and molding processability. Therefore Freqtis® is widely used for surface mounted electronic components. In .. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Vyncolit X655/1 Glass Fiber and Mineral Filled Novolac Phenolic Novolac resin based, glass fiber and mineral filled. High dimensional stability and excellent chemical resistance at high temperatures in hydraulic brake fluids. Used in particular in the ABS system.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D638 |
A. Schulman PP 984 Polypropylene Medium Impact Polypropylene DescriptionPolypropylene PP 984 is a medium impact polypropylene used primarily for automotive parts subjected to impact.Information provided by A. Schulman. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
DuPont Performance Polymers Crastin® SK645FR BK851 Polybutylene Terephthalate (PBT)
(Unverified Data**)&l 30% Glass Reinforced Flame Retardant Polybutylene Terephthalate Crastin SK645FR BK851 is a flame retardant 30% glass reinforced black polybutylene terephthalate molding resin. It is recognized as UL.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Eurotec® Tecomid® NA40 GR15 NL PA 6.6 15% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Flexural Strength | 180 MPa | 26100 psi | dry; ISO 178 |
Azoty Tarnow™ Tarnamid® T-27 GF20 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 20% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-30UH Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-35UH Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
BLUESTAR 101G30 PBT, 30% Glass Filled Typical Applications: Appliances, molded partsInformation provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-38H Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-38M Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-42H Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
Beijing Chemical Industry KAIFA® 301-G20F PBT Resin 20% glass fiber reinforced, flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |