Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 189 GPa @Temperature 316 °C |
27400 ksi @Temperature 601 °F |
Dynamic |
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 316 °C |
27400 ksi @Temperature 601 °F |
Dynamic |
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 538 °C |
27400 ksi @Temperature 1000 °F |
(heat treated at 1121°C (2050°F), water quenched plate) |
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 400 °C |
27400 ksi @Temperature 752 °F |
Dynamic |
Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750) Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 316 °C |
27400 ksi @Temperature 601 °F |
Dynamic |
Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 316 °C |
27400 ksi @Temperature 601 °F |
Dynamic |
Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
Modulus of Elasticity | 189 GPa @Thickness 12.7 mm, Temperature 538 °C |
27400 ksi @Thickness 0.500 in, Temperature 1000 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked Solution Treated, 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 189 GPa @Thickness 12.7 mm, Temperature 538 °C |
27400 ksi @Thickness 0.500 in, Temperature 1000 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 20% Cold Worked Solution Treated, 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 189 GPa @Thickness 12.7 mm, Temperature 538 °C |
27400 ksi @Thickness 0.500 in, Temperature 1000 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 30% Cold Worked Solution Treated, 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 189 GPa @Thickness 12.7 mm, Temperature 538 °C |
27400 ksi @Thickness 0.500 in, Temperature 1000 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 40% Cold Worked Solution Treated, 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 189 GPa @Temperature 23.0 °C |
27400 ksi @Temperature 73.4 °F |
|
Carpenter Thermo-Span® Fe-Co-Ni Superalloy Data provided by Carpenter Technology Corporation.Thermo-Span® alloy is a precipitation hardenable superalloy which exhibits a low coefficient of thermal expansion over a broad temperature range, h.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 316 °C |
27400 ksi @Temperature 601 °F |
Dynamic |
Haynes Hastelloy® G-35® Nickel Alloy Sheet, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
Modulus of Elasticity | 189 GPa @Temperature 316 °C |
27400 ksi @Temperature 601 °F |
Dynamic |
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |
|||
Modulus of Elasticity | 189 GPa @Thickness 12.7 mm, Temperature 538 °C |
27400 ksi @Thickness 0.500 in, Temperature 1000 °F |
(Heat treated at 1066°C (1950°F), rapid quenched, plate) |
HP Alloys Alloy B-2, Solution Treated, 50% Cold Worked Solution Treated, 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International. |
|||
Modulus of Elasticity | 189 GPa @Temperature 316 °C |
27400 ksi @Temperature 601 °F |
Dynamic |
Haynes Hastelloy® G-35® Nickel Alloy Bar, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |