Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 593 °C |
26400 ksi @Temperature 1100 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 593 °C |
26400 ksi @Temperature 1100 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 593 °C |
26400 ksi @Temperature 1100 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 593 °C |
26400 ksi @Temperature 1100 °F |
|
Haynes R-41 alloy, sheet 0.762-2.54 mm exclusive, 30 minutes at 1121°C, air cooled, aged 16 hours at 899°C Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
Modulus of Elasticity | 182 GPa @Temperature 593 °C |
26400 ksi @Temperature 1100 °F |
|
Haynes R-41 alloy, Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include .. |
|||
Modulus of Elasticity | 182 GPa @Temperature 538 °C |
26400 ksi @Temperature 1000 °F |
Heat treated at 1066°C, air cooled |
Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |