Polymer Property : Modulus of Elasticity = 24700 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, 20% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, 20% cold reduction, 925Â°C for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, 20% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, 40% cold reduction Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, 50% cold reduction, 980Â°C (1800Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 1000 hours exposure at 760Â°C (1400Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 1000 hours exposure at 980Â°C (1800Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, sheet, 32 hours exposure at 870Â°C (1600Â°F) Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa @Temperature 700 Â°C	24700 ksi @Temperature 1290 Â°F
Haynes 214Â® alloy, 10% cold reduction, 1095Â°C (2000Â°F) for 5 minutes Intended principally for use at temperatures of 955Â°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh ..
Modulus of Elasticity	170 GPa	24700 ksi	Filament property, in tension
Cytec Thornel® Mat VMA Carbon Fiber Data provided by the manufacturer, Amoco Performance Products, Inc.Composed of high strength, high modulus carbon filaments in a random-layered orientation. The fine diameter filaments are up to th..
Modulus of Elasticity	170 GPa	24700 ksi	Filament property, in tension
Cytec Thornel® Mat VMC Carbon Fiber Data provided by the manufacturer, Amoco Performance Products, Inc.Prepared by sectioning mat VMA into cubes ~ 0.5x0.5x1.0 in. VMC can be heterogeneously dispersed in matrix materials and thus enha..
Modulus of Elasticity	170 GPa	24700 ksi	Filament property, in tension
Cytec Thornel® Mat VME Carbon Fiber Data provided by the manufacturer, Amoco Performance Products, Inc.Form of mat VMA with shorter fibers for injection molding. Fiber lengths average 200 µm - inadequate for good mechanical property..
Modulus of Elasticity	170 GPa @Temperature 649 °C	24700 ksi @Temperature 1200 °F
ATI Allegheny Ludlum AL 625HP™ Stainless Steel Nickel-based superalloy. Characteristics:exceptional fatigue resistance, excellent resistance to oxidation and corrosion, outstanding strength and toughness over a range of temperatures from cryogen..