Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Creep Modulus, 1 hour | 1400 - 2800 MPa | 203000 - 406000 psi | Average value: 2130 MPa Grade Count:16 |
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim.. |
|||
Tensile Creep Modulus, 1 hour | 1400 - 2400 MPa | 203000 - 348000 psi | Average value: 2120 MPa Grade Count:9 |
Overview of materials for Polybutylene Terephthalate (PBT), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Extrusion Grade". Each property range of values reported is minimum an.. |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | |
Arkema Group Oroglas® DRM Acrylic, Extrusion Grade
(discontinued **) OROGLAS DRM is an extrusion grade that offers the typical properties of high impact acrylic combined with matte surface finishing.OROGLAS DRM is recommended for extrusion of sheets for lighting, pr.. |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | |
Arkema Group Oroglas® DRT Acrylic, Impact Grade
(discontinued **) For extrusion and injection molding applications. OROGLAS DRT combines good thermal resistance with an excellent impact resistance.Key features : impact resistance: up to 10 times more impact-resis.. |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | |
Arkema Group Oroglas® HFI-10 Acrylic, Impact Grade
(discontinued **) OROGLAS HFI-10 is an impact grade that in addition to its superior impact resistance provides an improvement in flow which contribute to improve molding behavior and reduce cycle time.Key features :.. |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | ISO 899-1 |
Lanxess Pocan® S 1506 000000 PBT PBT, non-reinforced, injection molding extrusion, impact modified |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa @Time 3600 sec |
203000 psi @Time 1.00 hour |
50%RH; ISO 899-1 |
DuPont Performance Polymers Zytel® FG101L NC010 Nylon 66
(Unverified Data**) Unreinforced Polyamide 66 with Developed for Food Contact ApplicationsZytel FG101L NC010 is a lubricated polyamide 66 resin for injection molding. It has been developed for consideration into applic.. |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa @Temperature 23.0 °C |
203000 psi @Temperature 73.4 °F |
50%RH; ISO 899 |
DuPont Performance Polymers Zytel® FG101L NC010 Nylon 66
(Unverified Data**) Zytel® FG101L NC010 is a lubricated polyamide 66 resin for injection molding. It has been developed for consideration into applications such as parts for the food industry.Information provided by D.. |
|||
Tensile Creep Modulus, 1 hour | 1400 - 2700 MPa | 203000 - 392000 psi | Average value: 2350 MPa Grade Count:4 |
Overview of materials for Acrylic, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Extruded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | |
Arkema Group Oroglas® SG 10 Acrylic, Gamma Radiation Resistant
(discontinued **) OROGLAS SG 10 is special Gamma - radiation - resistant formulation designed for use in medical devises.OROGLAS SG 10 maintains exceptional clarity after 5 megarads of Gamma radiation with no advers.. |
|||
Tensile Creep Modulus, 1 hour | 1400 MPa @Time 3600 sec |
203000 psi @Time 1.00 hour |
50%RH; ISO 899-1 |
DuPont Performance Polymers Zytel® 101F NC010 Nylon 66
(Unverified Data**) Unreinforced Polyamide 66Zytel 101F NC010 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont .. |