Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 0.700 MPa | 102 psi | at 5% deformation |
Pyrotek I-14 Insulating Board Pyrotek's I-14 is a low density hydrous calcium silicate board which features exceptional strength and low thermal conductivity. Inorganic and incombustible, I-14 also contains no RDF's.A.. |
|||
Compressive Strength | 0.700 - 1.30 MPa | 102 - 189 psi | Cold Crushing Strength |
Gouda Vuurvast GI 23 Insulating Refractory Brick This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast. |
|||
Compressive Strength | 0.700 MPa | 102 psi | perpendicular to plane; ASTM D1621 |
SABIC Innovative Plastics ULTEM Foam XP060 PEI ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The .. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SF-100H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SF-101H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-101 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-201 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-202 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SF-100H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SF-101H Expandable Polystyrene (EPS) FR Characteristics: High Strength, High ExpansionTypical Application : InsulationInformation provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-101 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-201 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | @ 15 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
Samsung Cheil Industries Starex® SG-202 Expandable Polystyrene (EPS) High Expansion Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries. |
|||
Compressive Strength | 0.700 MPa | 102 psi | Cold Crush Strength; ASTM C133 |
BNZ Materials BNZ-20 Insulating Firebrick BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirem.. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® R63.80 Damage Tolerant Foam AIREX® R63 is a closed-cell, linear, thermoplastic polymer foam with extremely high damage tolerance. This formula combines high elongation and excellent bond strength. AIREX® R63 is cold formable.. |
|||
Compressive Strength | 0.700 MPa | 102 psi | average; perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® R82.60 High Performance Structural Foam AIREX® R82 is a closed-cell, thermoplastic polymer foam that combines fire resistance with low smoke and toxicity, along with good dielectric properties. It has a good strength to weight ratio, ver.. |
|||
Compressive Strength | >= 0.700 MPa | >= 102 psi | perpendicular to plane; ISO 844 |
3A Composites Core Materials AIREX® T90.60 Easy Processing Structural FST Foam AIREX® T90 is a closed-cell, thermoplastic and recyclable polymer foam with excellent fire, smoke & toxicity (FST) properties. It has very good mechanical properties and a good resistance to fatigu.. |
|||
Compressive Strength | 0.700 MPa @Strain 10.0 % |
102 psi @Strain 10.0 % |
DIN EN 826 |
BASF Styrodur® 5000 CS Extruded Rigid Polystyrene Foam (Europe) Description: Styrodur C is the green extruded rigid polystyrene foam (XPS) from BASF. As a thermal insulation, it makes a significant contribution to climate protection by reducing CO2 emissions. Th.. |