3A Composites Core Materials AIREX® R63.80 Damage Tolerant Foam

Category	Other Engineering Material , Composite Core Material , Polymer , Thermoplastic
Manufacturer	3A Composites Core Materials
Trade Name	AIREX®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3A Composites Core Materials AIREX® R63.80 Damage Tolerant Foam.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AIREX® R63 is a closed-cell, linear, thermoplastic polymer foam with extremely high damage tolerance. This formula combines high elongation and excellent bond strength. AIREX® R63 is cold formable to simple shapes and thermo-formable to complex three-dimensional curves, and is nonfriable. AIREX® R63 is a core material for dynamically loaded and shock absorbing sandwich structures.CharacteristicsGood impact strength (non-brittle failure mode)Easy to thermoform (cold and hot)Dimensionally stableExcellent fatigue resistanceOutstanding core-to-skin adhesionNon biodegradableGood sound and thermal insulationApplicationsMarine: Hull bottoms, hull sidesRoad and Rail: Front-ends, side skirts, crash beltsAircraft: Explosion proof cargo containersRecreation: Surf boards, canoes, kayaksIndustrial: Containers, shelters, helmets

Physical Properties	Metric	English	Comments
Density	0.0900 g/cc	0.00325 lb/in³	average; ISO 845
	0.0800 - 0.120 g/cc	0.00289 - 0.00434 lb/in³	typical range; ISO 845

Mechanical Properties	Metric	English	Comments
Tensile Strength	>= 1.20 MPa	>= 174 psi	in the plane; ISO 527 1-2
	1.40 MPa	203 psi	average; in the plane; ISO 527 1-2
Elongation at Break	>= 70 %	>= 70 %	shear; ISO 1922
	75 %	75 %	average; shear; ISO 1922
Tensile Modulus	>= 0.0450 GPa	>= 6.53 ksi	in the plane; ISO 527 1-2
	0.0500 GPa	7.25 ksi	average; in the plane; ISO 527 1-2
Compressive Strength	>= 0.700 MPa	>= 102 psi	perpendicular to plane; ISO 844
	0.900 MPa	131 psi	average; perpendicular to plane; ISO 844
Compressive Modulus	>= 0.0450 GPa	>= 6.53 ksi	perpendicular to plane; DIN 53421
	0.0560 GPa	8.12 ksi	average; perpendicular to plane; DIN 53421
Shear Modulus	>= 0.0180 GPa	>= 2.61 ksi	ASTM C393
	0.0210 GPa	3.05 ksi	average; ASTM C393
Shear Strength	>= 0.800 MPa	>= 116 psi	ISO 1922
	1.00 MPa	145 psi	average; ISO 1922
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²	DIN 53453

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.0370 W/m-K	0.257 BTU-in/hr-ft²-°F	ISO 8301

Descriptive Properties	Value	Comments
Color	brownish yellow